1) nonsupercon-ducting target
非超导靶
2) superconducting target
超导靶材
1.
We have prepared high-quality superconducting target with 100mm in diameter and 5mm in depth by soid-state reaction, The zero-resistance temperature of superconductor is 91k, the require of powders and technology of target heve been analysed.
本文利用固相反应成功地制备出直径Φ１００ｍｍ，厚度５ｍｍ的高质量超导靶材，超导靶材零电阻温度为９１Ｋ，同时对靶材原粉的要求和制靶工艺进行了分析。
3) high temperature superconducting target materials
高温超导靶材
4) nonsuperconducting
非超导
1.
It was found that small domains of nonsuperconducting phases RbxC(60)(x=4 and/or 6) tvers surrounded by the superconducting phase Rb3C(60) This was an important microstructral feature in the system.
在超导主晶相Ｒｂ３Ｃ（６０）中镶嵌某些非超导ＲｂｘＣ（６０）（ｘ＝４，６）微畴，形成此体系多相共存的显微结构特性。
5) non-magnetic superconductor
非磁性超导
1.
Temperature dependence of the coherent length ξ(T),critical velocity of Cooper pair vc(T),London penetration depth λ(T),critical current density j(T) for the non-magnetic superconductors LuNi2B2C、YNi2B2C,are studied in the vicinity of Tc by using a two-band G-L theory.
用二带G-L模型研究了非磁性超导LuNi2B2C和YNi2B2C的相干长度ξ(T)、速率vc(T)、伦敦穿透深度λ(T)和临界电流密度j(T)在Tc附近对温度T的依赖关系。
6) Y system high temperature superconductor
Y系高温超导靶材
补充资料：靶扫描和靶重建
靶扫描和靶重建
影像学术语。CT检查中，对扫描野(SFOV)中某一兴趣区扫描时行较大矩阵重建的方式称靶扫描。在扫描及影像重建完成后，对显示野(DFOV)中某一兴趣区重新进行较大矩阵重建成像的方式称靶重建。前者是直接利用扫描野中兴趣区的较大量的原始数据进行影像重建，后者则是利用常规扫描中采集的原始数据进行兴趣区的影像重建。两种技术实现的基本前提都是一次扫描所获得的投影测量数据必须能够满足兴趣区影像重建矩阵所需的信息量。靶扫描在扫描前预先设定兴趣区，成像后不储存非兴趣区原始数据；靶重建则需储存层面扫描所获得的全部原始数据，占用较多的磁盘空间，但以后可在图像中任选兴趣区进行局部重建。两种技术在成像效果(空间分辨率，对比分辨率)上是一致的，这与单纯的局部图像放大(zoom)不同。后者没有增加兴趣区内像素数量，虽使影像扩大但分辨率并未提高，清晰度反有下降。