1) Sm2Fe17 compound
Sm2Fe17化合物
1.
The changes in phase structure and Curie temperature of the Sm2Fe17 compound after nitrogen absorption were studied by using X-ray diffraction,differential thermal/thermo-gravimetric analyzer and magnetic measurement.
通过X-射线衍射、差热-热重(DTA-TG)联用仪以及磁测量等手段,研究了Sm2Fe17化合物吸氮后的相结构及居里温度的变化行为。
2.
The structure and magnetic properties of Sm2Fe17 compound and its nitrides were investigated by means of differential thermal/thermogravimetric analysis.
通过X射线衍射、差热-热重(DTA-TG)联用仪以及磁测量等手段研究了Sm2Fe17化合物及其氮化物的相结构和磁性。
2) Sm_2Fe_ 17-xCr_x compound
Sm2Fe17-xCrx化合物
1.
The structural and magnetic properties of Sm_2Fe_ 17-xCr_x compound have been investigated by means of x-ray diffraction and magnetization measurements.
对晶胞体积及晶胞参数的分析结果表明在Sm2Fe17-xCrx化合物中存在着较强的各向异性的磁体积效应。
3) Sm_2Fe_(17)-type alloy
Sm2Fe17型合金
1.
The microstructure,phase composition and magnetic properties of Sm_2Fe_(17)-type alloys and their nitrides with different Sm content were studied by means of powder metallurgy technique and air-tight nitrogenation.
通过采用粉末冶金法及密封氮化的方法,对添加不同钐含量的Sm2Fe17型合金及其氮化物的组织形貌、物相组成与结构及磁性能进行了研究。
4) Sm_2Fe_(17) alloy
Sm2Fe17合金
1.
Processing routes and important factors for preparing Sm_2Fe_(17) alloy by reduction-diffusion method have been studied in the paper, the theoretical analysis and experimental investigation of mechanism of reuction-diffusion have been carried out by XRD and SEM.
主要研究还原扩散法(R/D)制备Sm2Fe17合金的工艺和主要影响因素,并通过XRD和SEM等分析测试手段对还原扩散机理作了理论分析和实验研究,得出了还原扩散法制备Sm2Fe17的最佳工艺条件,实验表明在合理的原料配比条件下,1423K保温6小时后快淬可以制得成分单一的Sm2Fe17合金。
5) Sm_2Fe_(17)
Sm2Fe17
1.
Sm_2Fe_(17) and Sm_(10.
通过真空电弧炉制备了Sm2Fe17和Sm10。
6) Sm2Fe17 alloy precursor
Sm2Fe17合金前驱体
补充资料：Fe3Al基金属间化合物高温合金
Fe3Al基金属间化合物高温合金
Fe_(3)Al-base intermetallic compound superalloy
Fe3AI JIJ一nshujlon huahewu gaowen heJinFe3AI基金属间化合物高温合金(F e3AI一baseintermetallie eomPound suPeralloy)以Fe3AI相为基体的金属间化合物高温合金。该合金具有优异的高温抗氧化、抗硫化腐蚀性能，合金密度较小，因为不含贵重元素，故价格低廉，很适合于在高温氧化、硫化腐蚀的环境中工作。Fe3AI合金有两个不足之处:室温很脆，伸长率仅3%左右;高温强度不足。通过添加合金元素铬、硼，采取温加工工艺和合理的热处理制度，基本上解决了室温脆性问题，室温拉伸伸长率提高到15%左右。提高强度的途径是进行合金化，添加错、妮、铝等元素进行固溶强化和析出第二相进行时效强化，使合金室温拉伸强度达到l000MPa，600℃拉伸强度达到560MPa。Fe3AI基金属间化合物高温合金可以制造加热元件、炉子紧固件、热交换器、汽车用管材、石油管道和磁性元件等。该合金在真正走向实用之前，应在冶炼工艺和热加工工艺方面进行改进。 (}马培立卜