1) Critically tangential compression stress
临界切向压应力
3) critical compressive stress
临界压应力
1.
A calculation formula for the critical compressive stress is propose
本文运用能量法以锥形件拉深为例 ,分析了具有悬空区的轴对称零件发生内皱的临界条件 ,并进一步给出了临界压应力计算方
4) critical resolved shear stress (CRSS)
临界分切应力(CRSS)
5) critical resolved shear stress
临界分切应力
1.
Based on the micro-structural feature of single crystal Ni-base superalloy,two micro-models have been proposed to calculate and analyze its thermal misfit,especially,the critical resolved shear stress of the two-phase superalloys.
基于微胞模型，对两相合金的临界分切应力进行了分析，结果表明，宏观临界分切应力可用考虑热不协调性的有限元法来处理，所得结果还可推广到较大的γ’相体积分数ｆ的情况。
6) the critical shear stresses
临界抗剪切应力
1.
A direct calculation method of the critical shear stresses was established according to experiment datum on simulated rainfall.
提出了采用人工模拟降雨试验数据直接计算临界抗剪切应力的方法。
补充资料：临界分切应力
临界分切应力
eritical resolved shear stress
积为A/cos癸，滑移方向与拉伸轴的夹角为尺，如图所示。因此，F在此滑移面沿滑移方向的分切应力r为: r~Jeos职eos穴式中的cospcos只称为取向因子。对于面心立方晶格而言，有12个等同的滑移系统。晶体在拉伸过程中，究竟在哪一个系统上滑移取决于取向因子。取向因子最大的，优先滑移。当甲一90’时，即拉伸轴平行于滑移面时，或当穴一90a，即拉伸轴垂直于滑移面时，取向因子均为零，滑移不能进行。当沪和只处于同一平面且均为45。时，可以得到最大的取向因子和切应力。 l沾界分切应力定律的实质是:作用于单位长度位错线上促使位错滑移的力，决定于沿滑移面的切应力在滑移方向上的分量。当此切应力分量达到一定的临界值时，位错开始滑移。 l愉界分切应力而对于杂质、温度和形变速率相当敏感。材料的纯度愈高，即杂质愈少，而愈低;而少量杂质，不论在基体溶解与否，都会使而大幅度提高。低温时，肠随着温度的升高而显著降低，超过一定温度时变化不太显著，趋于稳定值。形变速率愈大，T0也愈高。(周浩孔庆平)临界分切应力eritical晶体中滑移要素的取向resolved shear stress外 力在晶体某一滑移面和滑 移方向上的分解切应力， 达到使晶体开始产生滑移 时的临界值。单晶体的拉 伸实验表明，一个滑移系 统只有当受到一定大小的 切应力时，它才能开始滑 移。这就是施密特 (Schlllid)的临界分切应 力定律。 设F为沿着拉伸轴方 向的拉力，A为试样的横 截面积，拉伸应力J一 F/A，滑移面法线与拉 伸轴的夹角为p，滑移面