1) Pyroelectric thin films
热释电薄膜
1.
Two kinds of multicomposition composite ungradient KTN pyroelectric thin films for high pyroelectric coefficient within broad temperature region were prepared via sol-gel method on the Pt/Ti/SiO2/Si substracts.
为使KTN热释电薄膜能够在较宽的温度范围内有较高的热释电系数,本文在Pt/Ti/SiO2/Si基片上采用Sol-Gel法制备了两种多组分成分非梯度分布的KTN热释电薄膜。
2) pyroelectric /ferroelectric thin film
热释电/铁电薄膜
3) multi layer pyroelectric thin film
复合热释电薄膜
1.
In order to reduce the thermal dissipation from the pyroelectric film to the substrate and meet the needs of integration with silicon, the multi layer pyroelectric thin film (MPTF) was introduced.
为解决热释电薄膜红外探测器中的热损失问题 ,引入了复合热释电薄膜的概念 。
4) pyroelectric composite film
热释电复合薄膜
5) BST pyroelectric thin film
BST热释电薄膜
6) pyroelectric thin film IR detector
热释电薄膜红外探测器
1.
Multilayer film that consists of porous silica layer integrated with silica buffer layer is used as thermal insulating structure for uncooled pyroelectric thin film IR detector.
采用由多孔 Si O2 薄膜和过渡 Si O2 薄膜组成的复合薄膜结构实现了非制冷热释电薄膜红外探测器的热绝缘 。
补充资料：晶体热释电效应
分子式：
CAS号：
性质：又称焦电效应。某些晶体由于结构上的不对称性，受温度变化引起某一结晶学方向上正负电荷重心的相对位移，改变自发极化状态，从而在该方向两边产生数量相等、符号相反的束缚电荷，即出现热释电效应。通常可分为两类：(1)具有自发极化，且自发极化不能为外电场转向的晶体，称为热释电晶体，如电气石、硫化钙、硒化钙、硫酸锂、氧化锌等；(2)自发极化可以为电场所转向的晶体，即铁电体，如硫酸三甘肽(TGS)、铌酸锂、钽酸锂、钛酸钡等。这些铁电晶体中的大多数可制成陶瓷(多晶体)，经极化处理后，能从各向同性体转变成各向异性体，并具有剩余极化，能像单晶体—样，显现热释电效应。由于陶瓷易加工，易于改性：成本低，是很有前途的热释电材料。利用晶体或陶瓷的热释电效应，可以制造红外热释电探测器、红外热释电摄像管等，在军事领域等已获应用。
CAS号：
性质：又称焦电效应。某些晶体由于结构上的不对称性，受温度变化引起某一结晶学方向上正负电荷重心的相对位移，改变自发极化状态，从而在该方向两边产生数量相等、符号相反的束缚电荷，即出现热释电效应。通常可分为两类：(1)具有自发极化，且自发极化不能为外电场转向的晶体，称为热释电晶体，如电气石、硫化钙、硒化钙、硫酸锂、氧化锌等；(2)自发极化可以为电场所转向的晶体，即铁电体，如硫酸三甘肽(TGS)、铌酸锂、钽酸锂、钛酸钡等。这些铁电晶体中的大多数可制成陶瓷(多晶体)，经极化处理后，能从各向同性体转变成各向异性体，并具有剩余极化，能像单晶体—样，显现热释电效应。由于陶瓷易加工，易于改性：成本低，是很有前途的热释电材料。利用晶体或陶瓷的热释电效应，可以制造红外热释电探测器、红外热释电摄像管等，在军事领域等已获应用。