1) ordered porous alumina
有序多孔氧化铝膜
2) electrochemically anodize
有序多孔氧化铝模板
3) ordered porous zinc oxide thin film
有序多孔氧化锌薄膜
4) Ordered mesoporous alumina
有序介孔氧化铝
1.
Preparation of ordered mesoporous alumina using a mixed template;
复合模板剂制备有序介孔氧化铝
2.
Ordered mesoporous alumina was synthesized by sol-gel method with isopropoxide alumina as the source of alumina and PEO-PPO-PEO block copolymer F127 as the template.
探讨了水铝比、醇水混合溶液的滴加速度、反应时间、水浴温度、陈化温度及陈化时间等条件对合成的有序介孔氧化铝结构的影响。
5) Organized mesoporous alumina
有序介孔氧化铝
1.
Synthesis and characterization of organized mesoporous alumina by nonionic template;
非离子模板剂制备有序介孔氧化铝及表征
2.
Structure and properties of nickel-containing catalysts supported on organized mesoporous alumina prepared by different supporting methods;
不同负载方法制备镍金属有序介孔氧化铝催化剂的结构及性能
3.
Synthesis of organized mesoporous alumina using an inorganic aluminum salt precursor;
无机铝盐制备有序介孔氧化铝及其表征
6) Porous alumina membrane
多孔氧化铝膜
1.
Nanometer-scale porous alumina membrane is prepared by anodic oxidization.
比较了电化学抛光前后铝片表面的微观结构,用阳极氧化法制备了纳米级多孔氧化铝膜,用扫描电镜研究分析了氧化铝膜孔的排列规律。
2.
Porous alumina membrane is prepared by aluminum anodizing in given acidic solution.
通过二次阳极氧化方法制备多孔氧化铝膜与一次阳极氧化方法制备多孔氧化铝膜孔排布规律性的对比 ,结果发现 ,二次阳极氧化方法制取的多孔氧化铝膜孔排布规律性明显好于一次阳极氧化法制取的多孔膜 。
补充资料：多孔膜
分子式：
CAS号：
性质： 指每平方厘米含有一千万至一亿个孔，孔隙率占总体积70％～80％，孔径均匀，孔径范围在0.02～20μm之间的分离膜。当膜的孔径大于5nm时称为微孔膜(microporous membrane)；孔径在1～5nm时称细孔膜(fine-pored membrane)，包括超滤膜和反渗透膜。
CAS号：
性质： 指每平方厘米含有一千万至一亿个孔，孔隙率占总体积70％～80％，孔径均匀，孔径范围在0.02～20μm之间的分离膜。当膜的孔径大于5nm时称为微孔膜(microporous membrane)；孔径在1～5nm时称细孔膜(fine-pored membrane)，包括超滤膜和反渗透膜。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。