1) surface height of welding pool
熔池表面高度
2) surface temperature of melt pool
熔池表面温度
1.
The surface temperature of melt pool in crucible and hearth of TC4 alloy during electron beam cold hearth melting was measured accurately by using M9100 pyrometer.
结果表明,结果表明,熔炼工艺参数如熔化速度、熔炼功率、电子束扫描方式和扫描频率都会对熔池表面温度产生剧烈影响。
4) melt pool height
熔池高度
1.
On the basis of the theoretical mathematical model developed, the influence of melt pool height on the solidification structure of twin-roll thin strip of 1Cr18Ni9Ti Stainless steel was predicted under the condition in which the thickness of thin strip was constant.
在已建立的理论数学模型的基础上,以1Cr18Ni9Ti不锈钢为研究对象,模拟预测了薄带厚度保持不变条件下熔池高度对薄带凝固组织的影响。
5) MIG weld pool
熔池表面形状
1.
It puts emphasis on analyzing how the droplet impact af fects the MIG weld pool geometry, and gives a set of algorithm to calculate weld reinforcement and weld pool geometry.
建立了熔化极惰性气体保护电弧焊(MIG)焊接熔地流场与热场的数值分析模型,分析了熔滴冲击力对MIG焊接熔池表面形状的影响规律,提出了计算焊缝余高部分和熔池几何参数的算法定量分析了熔滴到达熔池表面时,其冲击力对焊缝和熔地形状的影响。
补充资料:熔盐电化学表面合金化
分子式:
CAS号:
性质:其实质是熔盐中金属的电沉积和固态扩散合金化两种作用的综合。当在熔盐中使用活性较强的金属作为阳极,以活性较弱的金属作为阴极,并将阴、阳极连成回路,则形成一个自发的原电池。阳极在熔盐中溶解,其离子在阴极表面放电析出。与此同时,于高温下在基体(阴极)表面沉积的合金元素向内部扩散形成固溶体或金属间化合物的表面合金层。通过改变基体金属和被沉积金属,可以获得具有特殊性质的表面合金,性质远优于单个金属。铌、钽、铝、铍、硅等的表面合金化已在高技术领域中得到了应用。
CAS号:
性质:其实质是熔盐中金属的电沉积和固态扩散合金化两种作用的综合。当在熔盐中使用活性较强的金属作为阳极,以活性较弱的金属作为阴极,并将阴、阳极连成回路,则形成一个自发的原电池。阳极在熔盐中溶解,其离子在阴极表面放电析出。与此同时,于高温下在基体(阴极)表面沉积的合金元素向内部扩散形成固溶体或金属间化合物的表面合金层。通过改变基体金属和被沉积金属,可以获得具有特殊性质的表面合金,性质远优于单个金属。铌、钽、铝、铍、硅等的表面合金化已在高技术领域中得到了应用。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。
参考词条