1) ductile rare earth phase
延性稀土相
2) Rare Earth Phase
稀土相
1.
The experimental results show that the fatigue crack source is located either in rare earth phase at surface for unpeened specimens or in rare earth phase and slip zone beneath surface for shot-peened specimens.
结果表明,疲劳裂纹源在表面未强化试样表面稀土相处萌生,而对表面强化试样而言,疲劳裂纹源在表面强化层下稀土相处或滑放区萌生。
2.
The microstructure of EBW joints (Electron Beam Welding) of Ti-60 alloy and its rare earth phase distribution were investigated.
研究了Ti-60合金电子束焊接接头的显微组织及稀土相的分布特征;对焊接接头高温旋转弯曲疲劳性能进行了试验研究,讨论了影响接头疲劳性能的主要因素。
3) RE-rich phase
富稀土相
1.
7 alloy,but linear RE-rich phase appeared in.
文章阐述了稀土元素对该类高强度耐磨黄铜的组织和性能的影响,试验表明适量加入稀土会显著细化晶粒,过量的稀土会导致在合金显微组织中形成线形富稀土相。
4) Mg-RE phase
镁-稀土相
5) rare earth rich phase
稀土相
1.
Based on the binary alloy phase diagram analysis, Miedema theory(formation heat theory) is employed to explain the formation of rare earth rich phase.
本文基于对二元合金平衡相图的分析以及应用Miedema生成热模型对稀土相AlCe(AlLa)的形成进行了分析。
2.
Microstructure of rare earth rich phase of rapidly solidified (RS) TiAl based alloys was investigated.
利用两种不同的快速凝固方法对TiAl RE合金中稀土相的显微组织进行了研究并与铸态组织进行对比。
3.
The solidifies characterization of rare earth rich phase in slowly and rapidly cooled Ti 55 alloy was observed and analyzed.
Ｔｉ５５ 高温钛合金在缓冷（１０００ ｋｇ 铸锭冒口） 条件下， 正常凝固区中稀土相呈弥散分布状态，初始补缩区中稀土相聚集成团， 正常补缩区中稀土相颗粒沿平行于凝固界面方向规则排列； 在快冷（ 锤砧薄片） 条件下， 稀土相除弥散分布在合金中外， 出现稀土相颗粒排列成行的现象。