1) pigment's light-resistance
颜料光阻
2) fluorescent pigment
荧光颜料
1.
The dispersion and heat tolerance of several domestic and foreign fluorescent pigments in plastic were compared.
比较了国内外几种不同颜色的荧光颜料在塑料中的分散性和耐热性,发现进口K系列颜料的分散性和耐热性优于国产AX、FH系列颜料,随着温度的提高,颜料的分散性有所改善;大部分进口K系列颜料本身的耐热性及其在塑料中的耐热性优于国产AX、FH系列,而国产FH绿色荧光颜料的耐热性优于进口K系列的同颜色产品。
2.
In this paper, a kind of micro sphere fluorescent pigment with high solvent resistancewas prepared by using two-approachs method, and the benzene substitutedmelamine-formaldehyde-melamine copolymer(BMFM) was employed as carrier resin.
本文采用分段合成工艺制得了微球形耐溶剂荧光颜料复合体系，采用改性苯代三聚氰胺-甲醛-三聚氰胺三元共聚物作为载体树脂。
3.
The color conversion film is prepared by dispersing a red fluorescent pigment VQ-D25 into the epoxy resin.
利用荧光效率高、色稳定性好的N-BDAVBi材料作为发光掺杂剂,掺入主体材料CBP中得到蓝色发光层,制备了结构为:ITO/NPB/CBP:NBDAVBi/BPhen/LiF/Al的蓝光OLED;然后与红色有机荧光颜料VQ-D25制备的色彩转换膜相结合,通过优化转换膜的厚度(2000nm)和荧光颜料的掺杂比例(11%)来调整器件的发光光谱,制备了一种新型的WOLED器件,在9V工作电压下,白光器件的CIE色坐标为(0。
3) nacreous pigment
珠光颜料
1.
For thesake of knowing mechanism of preparing nacreouspigment of mica titanium and adjusting pH with urea, we need to measure fast and exactly concentration of titanium to direct preparing top grade nacreous pigment of mica titanium.
为了更好地了解尿素中和法制备云母钛珠光颜料过程中钛水解的机理,指导高档次云母钛珠光颜料的制备,需要对该过程中钛的含量进行准确快速的测定,本文对过氧化氢分光光度法测定钛的方法进行了实验研究。
2.
TiO2 - mica nacreous pigment with Fe2O3 is prepared by the process of boiling hydrolysis.
采用沸腾水解法制备三氧化二铁包膜云母钛珠光颜料。
4) Pearlescent pigment
珠光颜料
1.
Study on the technology of basic lead carbonate pearlescent pigment by pushing process and inversing phase method;
碱式碳酸铅珠光颜料的挤水转相工艺研究
2.
The current study on improving the characteristics of mica pearlescent pigment using the surface modification;
云母钛珠光颜料表面改性研究现状
3.
New progress and preparation methods for pearlescent pigment;
珠光颜料的研究方法与新进展
5) luminescent pigment
发光颜料
1.
A luminescent plastics was prepared by adding zinc sulfide(ZnS) or alkaline earth aluminate luminescent pigments in polyproplene.
分别将ZnS类发光颜料及碱土铝酸盐类发光颜料加入到聚丙烯中,制成ZnS发光塑料和碱土铝酸盐发光塑料,测定其辉度、余辉时间及光稳定性。
2.
Silica encapsulation was studied on the particle surface of aluminate-based luminescent pigment by using TEOS as the raw materials.
采用四乙氧基硅(TEOS)为硅包膜剂,在SrAl2O4:Eu2+,Dy3+发光颜料颗粒表面进行包膜,通过扫描电镜(SEM)、粒度测量、BET比表面积测试及X射线光电子能谱(XPS)分析,证实发光颜料颗粒表面包覆了一层厚度约为14nm的致密均匀的SiO2纳米膜。
3.
The luminescent features of fluorescent substance applied in energy accumulating and luminescent pigments are elaborated.
介绍了发光材料及其分类,详述了蓄能发光颜料用荧光体的发光特性,对其发光性能进行了比较。
6) luminous pigment
发光颜料
1.
This article has reviewed the composition, physical properties, mechanism of luminous performance, preparation and surface modification technologies and application of the title earth alkali alumino silicate based long afterglow luminous pigment activated by rare earth ions, and discussed the development trend and prospect of this luminous pigment.
综述了稀土离子激活碱土铝酸盐长余辉发光颜料的组成与物性、发光机理、制备与表面改性技术及其应用 ,并根据其研究现状 ,探讨了碱土铝酸盐体系长余辉发光颜料的研究方向和发展前景。
补充资料：颜料保光性
分子式：
CAS号：
性质：是指添加有颜料的应用系统，特别是色漆涂膜，能抵抗由于暴露在大气中受大气和各种因素影响而失去光泽的能力。以失光百分率表示(以原始光泽为100)，共分0～4级五个级别，失光率分别为<5％(0级)，6％～20％(1级)，21％～50％(2级)，51％～80％(3级)，>80％(4级)。颜料应用系统失光主要由基料和颜料的性能决定的。高光泽涂料，特别是汽车面漆，要求最大的保光性，涂膜应当长期具有非常高的鲜映性或映象强度，对这种系统，要求用高光泽、无光雾、高分散性、高耐久性的颜料，配以高档基料。化钛水溶液在较高温度(150～300℃)和与温度相对应的较大压力下的反应器内进行水热反应，是正在探索的一种颜料制备法。
CAS号：
性质：是指添加有颜料的应用系统，特别是色漆涂膜，能抵抗由于暴露在大气中受大气和各种因素影响而失去光泽的能力。以失光百分率表示(以原始光泽为100)，共分0～4级五个级别，失光率分别为<5％(0级)，6％～20％(1级)，21％～50％(2级)，51％～80％(3级)，>80％(4级)。颜料应用系统失光主要由基料和颜料的性能决定的。高光泽涂料，特别是汽车面漆，要求最大的保光性，涂膜应当长期具有非常高的鲜映性或映象强度，对这种系统，要求用高光泽、无光雾、高分散性、高耐久性的颜料，配以高档基料。化钛水溶液在较高温度(150～300℃)和与温度相对应的较大压力下的反应器内进行水热反应，是正在探索的一种颜料制备法。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。