4) bubble
[英]['bʌbl] [美]['bʌbḷ]
气泡，水泡
5) skin blowhole
皮下气泡
1.
The forming reasons of the skin blowhole in welding gas cylinder steel HP295 are analyzed.
分析了HP295焊接气瓶用钢铸坯皮下气泡缺陷的成因;明确了钢液的过热度及脱氧合金化是铸坯产生皮下气泡的主要影响因素;提出了相应的防止措施。
2.
For bearing steel GCr15,by using low times test and making an observation and analysis of microstructure,it can be seen that the surface crack of billet results from skin blowhole and nonmetal lard.
针对GCr15轴承钢 ,通过低倍检验与显微组织的观察和分析 ,确定方坯的表面裂纹主要是由钢锭中的皮下气泡和非金属夹杂物所引
6) subcutaneous bubble
皮下气泡
1.
It is suggested that the inclusions,the content of oxygen and the subcutaneous bubble emerged after rolling are the main reasons which result in bend crack of strip steel.
针对带钢在加工使用过程中出现的弯裂现象,对于两种不同厚度规格出现弯曲开裂现象的带钢进行了金相分析、气体含量分析和SEM分析,认为带钢中夹杂物含量,钢中氧含量,以及皮下气泡经轧制后暴露是引起带钢弯裂的主要原因。
2.
It is suggested that this defect is originated from the internal crack and the subcutaneous bubbles of billet,as well as unreasonable pass design of roughing mill.
通过对试样进行金相分析,对铸坯表面修磨试验结果分析及对连铸坯在高线粗轧第1道和第2道轧制的受力和变形的分析,发现盘条表面的一种特殊的线状缺陷形成的原因是连铸坯存在边内裂和皮下气泡,粗轧机组(特别是第1和第2架)孔型设计不合理,也促进这种线状缺陷的形成。