1) H ∞ loop-shaping technique
H∞环路成形技术
2) H ∞ loop shaping technique
H~∞环路成形技术
3) H∞ loop shaping
H∞环路成形
1.
A mixed optimization algorithm is proposed for an inverted pendulum based on genetic algorithm (GA) and H∞ loop shaping theory .
提出了基于遗传算法(GA)和H∞环路成形理论混合优化的倒立摆控制方法。
2.
H∞ controller was designed by H∞ loop shaping procedure, and the method for selecting the parameters of compensator based on GA and pseudo diagonalization was provided.
运用H∞环路成形理论设计控制器。
4) Loop-shaping H∞ control
环路成形H∞控制
5) H_∞ closed-loop gain shaping control techniques
H∞闭环增益成形控制技术
6) H_∞ loop shaping
H∞回路成形
1.
The problem of H_∞ loop shaping attitude stabilization control for Tracking and Data Relay Satellite(TDRS) is investigated.
主要研究中继卫星H∞回路成形姿态稳定控制问题。
2.
Based on the introduction and analysis of the approach of H_∞ loop shaping,aiming at the problems that the weight functions are chosen by trial and error,and the synthetical performance index of the controller is hard to meet the frequency and time domain performance requirements,an improved weight function selection method is proposed based on engineering design and chaos optimization.
在介绍和分析H∞回路成形基本设计方法的基础上,针对权重函数选取需要反复迭代、过程繁琐、所得控制器难以同时满足时域和频域性能指标等问题,提出了一种基于工程设计、辅以混沌优化理论的权重函数选取方法。
补充资料：主要射出成形材料成形时应注意事项
■主要射出成形材料成形时应注意事项
品 名 注 意 事 项
PVC
聚氯乙烯
1. 产品种类范围非常广（硬质、软质、聚合物等），成型条件各有不同，从熔融至分
解之温度范围很小，尤须注意加热温度。
2. 附着水分少，但成型周期尽可能减少（50℃~60℃热风干燥）。
3. 成型机方面，与材料直接接触的部位须电镀或采用不锈钢以防热分解所产生的盐酸
侵蚀。射出压力2100kg/cm2程度。
4. 所有塑料当中必须是细心注意温度调节。
5. 浇口附近易产生流纹，故射出操作后，柱塞不要后退使浇口充分固化后再瞬间退后为宜。
6. 加热之初温不宜高，特别注意熔融情形。第二级加热温度较高，且尽可能使成形周
期缩短，比较安全。
PA
聚醯胺树脂
1. 成型温度比其它材料高，故采用油加热的成形机较适当。
2. 吸湿性大，必须充分干燥。水分对成型品的品质影响甚大（80℃热风干燥约5~6小时）。
3. 须退火以消除内部歪斜。
PP
聚丙烯
1. 同PE，但成形温度必须较高。熔融温度170℃，超过190℃则流动性大增，则毛边增加，
易产生接缝及凹入情形。
PC
聚碳酸脂
1. 吸湿性比尼龙小，但若有些微之水分存在则成型品产生其它色泽或气泡，故必须密封
干燥同时成形时也须预备干燥（120℃之温度4小时）。
2. 加热温度超过320℃时则产生热分解，成品变色，故特别注意温度调节，又成型时的温度调节也非常重要，须特别注意其最低温度、最低时间。
3. 须退火以消除内部歪斜（130℃~135℃，1小时程度为准）。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。