1) Medicinalfibroin membrane
药物丝素膜
2) Silk fibroin protein membrane
丝素膜
1.
The silk fibroin protein membrane is an amphoteric ion-exchange membrane composed of both weak acidic and weak basic groups.
研究了丝素膜的带电特性 ,其等电点在pH 4。
3) fibroin membrane
丝素膜
1.
Investigates the effects of epoxide molecular weight and dose and catalyst dose on the major physico_chemical properties of fibroin membrane by using cross linkers of epoxides with different molecular weight in the membrane preparation.
采用自行研制的不同分子量的环氧化合物作为制备丝素膜的交联剂 ,探讨了环氧化合物分子量及环氧化合物添加量、催化剂用量对丝素膜主要理化性能的影响。
2.
Fibroin membrane surface was actived by the plasma processing,and then grafted with heparin via glutaraldehyde,from which the fibroin membrane has anticoagulating ability.
利用等离子体处理技术使丝素膜表面被激活,以戊二醛作为交联剂,接枝肝素分子进行丝素膜表面抗凝血性修饰,从而为新型抗凝血生物医用材料的设计及临床应用提供试验依据。
3.
The loss percentage of fibroin membrane decreases after adding appropriate amount of rare earth into it.
丝素蛋白和稀土溶液的互溶与溶液的pH值具有一定的相关性 ,在丝素膜中加入适量稀土后溶失率下降 ;采用红外吸收光谱、X 射线衍射、热分析等实验手段进行测试 ,结果证明 ,稀土与丝素间存在着配位作用 ,丝素膜聚集态结构发生了相应的变
4) Silk fibroin membrane
丝素膜
1.
A kind of silk fibroin membranes were prepared by blend the PEGO and silk fibroin.
选用六种不同分子量的聚乙二醇与丝素共混制膜，并选用其中五种合成了五种不同分子量的聚乙二醇缩水甘油醚(PEGO)，以合成的PEGO为添加剂，研究了不同分子量、不同含量下制得的改性丝素膜的结构与性能。
5) fibroin film
丝素膜
1.
Describes the preparation,physical property and medicine releasability of the traditional Chinese medicine fibroin film.
介绍了中药丝素膜的制备方法及其物理性能和释药性能。
2.
It is studied that crystalline morphology and strength and stretch of the fibroin films are influ-enced by both temperature and dampness as the fibroin films are formed, the feeling of hand is alsoinvestigated in this paper.
本文研究了成膜温度与湿度对丝素膜的结晶形态及强力伸度的影响,对其手感亦进行了考察。
3.
Objective To investigate the effect of regenerated silk fibroin film on the attachment and growth of olfactory enshathing cells(OECs).
目的 观察新生大鼠嗅鞘细胞在再生丝素膜上的生长情况 ,探讨再生丝素膜在嗅鞘细胞移植修复脊髓损伤中成为细胞培养基质的可能性。
6) Silk membrane
丝素膜
1.
Methods Recalcification test, hemolysis test and platelet adhesive test were conducted for compact silk membrane, polyporous silk membrane, bovine pericardium and collagen sponge.
目的 了解丝素膜的血液相容性。
2.
Porous silk membrane, SD-1 silk membrane, epoxide silk membrane and bovine pericardium were repaired in rabbits.
目的：了解丝素膜血液相容性；通过动物实验，观察多孔丝素膜、SD-1丝素膜、环氧丝素膜三种材料和对照材料牛心包，植入后与下方的脑组织有无粘连、炎症反应极其程度，并进行比较；了解丝素膜的组织相容性，探讨其成为人硬脑膜修补材料的可行性。
补充资料：电解食盐水溶液离子膜电解槽所用的膜材料之一
分子式：
CAS号：
性质：又称全氟羧酸-磺酸复合离子膜 Rf-COOH-Rf-SO3H 电解食盐水溶液离子膜电解槽所用的膜材料之一。使用时，将较薄的羧酸层面向阴极，较厚的磺酸层面向阳极，因而兼有羧酸膜和磺酸膜的优点。由于Rf-COOH层的存在，可阻挡氢氧离子返迁移到阳极室，确保了高的电流效率（96%），因Rf-SO3层的电阻低，能在高电流密度下运行，且阴极液可用盐酸中和，产品氯气中氧含量低，氢氧化钠浓度可达33%～35%。可在全氟磺酸膜上涂敷一层全氟羧酸的聚合物，或是将磺酸膜和羧酸膜进行层压，或是采用化学方法处理而制得的复合膜。现以采用化学方法处理者质量最佳。
CAS号：
性质：又称全氟羧酸-磺酸复合离子膜 Rf-COOH-Rf-SO3H 电解食盐水溶液离子膜电解槽所用的膜材料之一。使用时，将较薄的羧酸层面向阴极，较厚的磺酸层面向阳极，因而兼有羧酸膜和磺酸膜的优点。由于Rf-COOH层的存在，可阻挡氢氧离子返迁移到阳极室，确保了高的电流效率（96%），因Rf-SO3层的电阻低，能在高电流密度下运行，且阴极液可用盐酸中和，产品氯气中氧含量低，氢氧化钠浓度可达33%～35%。可在全氟磺酸膜上涂敷一层全氟羧酸的聚合物，或是将磺酸膜和羧酸膜进行层压，或是采用化学方法处理而制得的复合膜。现以采用化学方法处理者质量最佳。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条