1) crack_tip asymptotic field
![点击朗读](/dictall/images/read.gif)
裂纹尖端渐近解
2) high-order crack-tip asymptotic fields
![点击朗读](/dictall/images/read.gif)
裂纹尖端高阶渐近场
3) crack tip
![点击朗读](/dictall/images/read.gif)
裂纹尖端
1.
Damage analysis of crack tip zone in metal sheets;
![点击朗读](/dictall/images/read.gif)
金属板材中裂纹尖端区的损伤分析
2.
Research of crack tip damage for metals material;
![点击朗读](/dictall/images/read.gif)
金属材料裂纹尖端损伤研究
3.
The electromagnetic stress on the crack tip in metal plate with strong current;
![点击朗读](/dictall/images/read.gif)
导电薄板内裂纹尖端区域的电磁应力
4) crack-tip
![点击朗读](/dictall/images/read.gif)
裂纹尖端
1.
Laser speckle interferometry was applied to obtain full field crack-tip displacements of steel fiber reinforced concrete specimens subjected to 3-point bending.
5%的钢纤混凝土三点弯曲裂纹试件的裂纹尖端位移场进行了测试,并换算为应变场。
2.
It is considered that the crack-tip lies on the interface of two phases media.
![点击朗读](/dictall/images/read.gif)
考察裂纹尖端位于两相介质界面的情况。
3.
The strain fields in damage zone around crack-tip are measured for differ- ent strain hardening exponent material specimens with double edge cracks using digital speckle correlation technique.
本文用数字散斑相关方法测量了五种不同幂硬化指数韧性金属材料(铝和铜),双边裂纹尖端细观区域内应变场。
5) crack tip asymptotic fields
![点击朗读](/dictall/images/read.gif)
裂尖渐近场
6) solution of near tip crack for Mode IIIcrack
![点击朗读](/dictall/images/read.gif)
Ⅲ型裂纹尖端场的解
补充资料:裂纹尖端张开位移
分子式:
CAS号:
性质:在外载荷的作用下,裂纹尖端两表面间的张开位移。用符号δ表示。由于在弹塑性条件下,已得到δ与工作应力σ(或应变ε)以及裂纹尺寸a(裂纹的半长)之间的关系,因此它是弹塑性断裂力学中的一个重要参量。
CAS号:
性质:在外载荷的作用下,裂纹尖端两表面间的张开位移。用符号δ表示。由于在弹塑性条件下,已得到δ与工作应力σ(或应变ε)以及裂纹尺寸a(裂纹的半长)之间的关系,因此它是弹塑性断裂力学中的一个重要参量。