1) magnetism/Incoloy 800H cracking tube
磁性/Incoloy 800H裂解管
2) Incoloy 800 H
Incoloy 800H
1.
The research shows that the elevated-temperature fracture toughness of Incoloy 800 H material for in-service furnace tubes falls down with rising temperature.
研究表明,服役炉管材料Incoloy 800H高温断裂韧性随温度升高而下降,在680℃下约为80～100 kJ／m2,550℃下断裂韧性值更高,试验结果为服役炉管高温短时断裂安全评估提供了重要依据。
3) 800H alloy
Incoloy 800H合金
1.
The failure problem of 800H alloy expansion joint bellow of ethylbenzene hydrogen removal system for styrene unit was analyzed in detail.
对苯乙烯装置乙苯脱氢系统Incoloy 800H合金膨胀节波纹管的失效问题进行了详细的分析,阐述了其失效的原因与机理,并提出了防护对策。
4) incoloy800H stainless steel
Incoloy 800H不锈钢
5) magnetic resolution
磁性离解
6) pyrolysis performance
裂解性能
1.
Evaluation on pyrolysis performance of natural gas liquid;
吐哈稳定轻烃裂解性能评价
2.
Evaluation on pyrolysis performance of feedstock for ethylene-making;
制乙烯原料油裂解性能评价
3.
Evaluation on pyrolysis performance of byproduct low carbon hydrocarbons and low octane number oils from refinery;
对炼油厂副产低碳烃及低辛烷值油品的裂解性能评价
补充资料：磁性材料2．薄膜磁性材料
磁性材料2．薄膜磁性材料
Magnetie Materials 2.Thin Film
在一定外加磁场作用下，其反磁化畴(磁矩取向与外磁场方向相反的畴)变为圆柱形磁畴。从膜面上看，这些柱形畴好像浮着的一群圆泡，故称磁泡或叫泡踌(另见磁性材料2.昨晶态磁性材料)。在特定的电路图形、电流方向和一定磁场情况下，可做到控制材料中磁泡的产生、传翰和消失，实现信息的储存和逻辑运算的功能。磁泡的直径在微米量级(0 .5~5协m)，每个磁泡的迁移率在1 .26~12.6em八s·A/m)〔 102一i03cm八s·oe)〕，因而可制成存储密度为兆位/cmZ(Mbit/cmZ)和数据处理速率为兆位/s(M肠t/s)的运算器件。磁泡器件经过近20年研究和开发，已取得广泛的实际应用。 对磁泡材料的主要要求是:(l)各向异性常数凡>粤斌，磁化强度从>外磁场强度H;(2)杂质缺陷小，2一~”~’.J泌~-一‘产’~~一~一’、~尹一~~~’J”均匀性好。目前研究得比较清楚的有铁氧体单晶薄膜和稀土一过渡金属薄膜。从制备工艺和性能稳定、器件开发等情况看，以铁氧体磁泡材料比较成熟，早期是用钙钦石型铁氧体单晶片来作磁泡材料，后为YIG单晶薄膜所取代。它是用液相外延法在Gd3Ga5OI:(简称GGO)基片上生成的单晶薄膜，其厚为微米量级。表4为稀土石榴石R3FesolZ的磁性;表5为一些磁泡材料的基本特性数值。农4稀土石抽石R.Fe‘ol，的磁性┌───────────┬────┬────┬────┬────┬────┬────┬────┬────┬─────┬────┬────┐│R │Y │Sm │EU │Gd │Tb │Dy │、Ho │Er │T】11 │Yb │Lu │├───────────┼────┼────┼────┼────┼────┼────┼────┼────┼─────┼────┼────┤│补偿温度，~p，K │ 560 │ 560 │ 570 │ 290 │ 246 │ 220 │ 136 │ 84│4
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条