1) composite thermal protection tile
金属复合防热瓦
1.
In this paper,the structure, manufacturing process and thermophysical properties of metallic composite thermal protection tile have been studied with prominent progression.
本文主要研究了,金属复合防热瓦的结构、制造工艺及热物理性能,并取得突破性进展。
3) complex metal
复合金属
1.
The paper introduces the manufacture,application and developement prospect of a novel complex metal for heat sink.
介绍了新型热沉用复合金属材料的设计、制造、应用技术及发展前景。
5) bimetal hot forging compound die
双金属复合热锻模
6) bimetal compound
双金属复合
1.
Selecting cast aluminum alloy and cast steel as inner loop and outer loop of the bimetal compound casting respectively, the casting was produced by induction heating in mold.
双金属复合铸件外圈采用铸造铝合金,内圈选取碳素结构钢,采用型内感应加热工艺进行复合。
2.
A good metallurgical combination at interface of bimetal compound casting was obtained.
双金属复合铸件外层采用铸造铝合金,内层选取碳素结构钢,采用型内感应加热工艺进行复合。
补充资料：防热功能复合材料
分子式：
CAS号：
性质：复合材料的耐热性主要取决于基体材料的耐热性能。通常可分为四个温区。(1)在200℃以下，复合材料的基体树脂最常用的有环氧、不饱和聚酯、酚醛等热固性树脂，其相应助剂也应有利于耐热性。(2)在200～300℃温区，基体树脂可采用热塑性树脂，如聚酰亚胺、聚醚醚酮、聚砜、聚苯硫醚、聚碳酸酯、聚醚砜等，增强纤维和助剂要考虑抗氧化性能，但热塑性树脂为基体的复合材料成型工艺技术比较复杂。另外，热固性树脂中的高性能环氧树脂、双马树脂和聚酰亚胺树脂，耐热性可达200～300℃，也可使用。(3)在300～700℃温区下，一般皆采用金属材料为基体(如铝、镁、钛等)，增强纤维也应考虑耐高温和与基体的相容性。如硼/铝、碳榴复合材料，均可在300～400℃温度下工作；碳化硅/钛复合材料可在550℃下工作。(4)在700℃以上，只有陶瓷基复合材料，包括碳基复合材料。碳微化硅、碳化硅/氮化硅等复合材料可在1000℃左右长期工作。抗氧化碳微复合材料可在1300℃左右长期工作。
CAS号：
性质：复合材料的耐热性主要取决于基体材料的耐热性能。通常可分为四个温区。(1)在200℃以下，复合材料的基体树脂最常用的有环氧、不饱和聚酯、酚醛等热固性树脂，其相应助剂也应有利于耐热性。(2)在200～300℃温区，基体树脂可采用热塑性树脂，如聚酰亚胺、聚醚醚酮、聚砜、聚苯硫醚、聚碳酸酯、聚醚砜等，增强纤维和助剂要考虑抗氧化性能，但热塑性树脂为基体的复合材料成型工艺技术比较复杂。另外，热固性树脂中的高性能环氧树脂、双马树脂和聚酰亚胺树脂，耐热性可达200～300℃，也可使用。(3)在300～700℃温区下，一般皆采用金属材料为基体(如铝、镁、钛等)，增强纤维也应考虑耐高温和与基体的相容性。如硼/铝、碳榴复合材料，均可在300～400℃温度下工作；碳化硅/钛复合材料可在550℃下工作。(4)在700℃以上，只有陶瓷基复合材料，包括碳基复合材料。碳微化硅、碳化硅/氮化硅等复合材料可在1000℃左右长期工作。抗氧化碳微复合材料可在1300℃左右长期工作。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。