1) Hydrous RuO_2
水合二氧化钌
2) hydrous ruthenium oxide
水合氧化钌
1.
The results indicate that hydrous ruthenium oxide particles in an amorphous phase were deposited homogeneously on MWNTs.
本文采用超声波技术合成了水合氧化钌/多壁碳纳米管纳米复合材料(Ru-MWNTs)前驱物,在150℃下热处理15h后得到Ru-MWNTs。
3) Ruthenium dioxide
二氧化钌
1.
Experiment results indicate that in process of preparing hydrate of ruthenium dioxide by hydrolyzing chlororuthenium acid many factors such as conentration of hydrolytic ruthenium ,temperature and pH value have influence on RaO2 productivity, specific suface, square resistance and temperature coefficient of resistance.
氯钌酸水解制备水合二氧化钌过程中，水解浓度、温度、ｐＨ值、洗涤对产率、比表面、方阻值、电阻温度系数都有影响，但终点ｐＨ值是影响二氯化钌性能的主要因素。
4) RuO2·xH2O
二氧化钌
1.
Several different proportions of composite electrodes were fabricated with the RuO2·xH2O and active carbon, and tested in their electrochemical performances and physical characteristics.
用sol-gel法制备了水合二氧化钌,进而制备了二氧化钌/活性炭复合电极,并对各种不同配比的复合电极的电化学性能和物理性能进行了实验研究。
5) RuO_2
二氧化钌
1.
Improvement of water washing technology in preparation of RuO_2.;
二氧化钌水洗工艺的改进
2.
And RuO_2·xH_2O powders was prepared by using RuCl_3 and NaOH as raw materials.
用醋酸锰和高锰酸钾制备二氧化锰粉末：用氯化钌和氢氧化钠制备水合二氧化钌粉末。
6) RuO2
二氧化钌
1.
In order to improve the performances of electrode materials for super-capacitors, multi-element composite electrodes were prepared using RuO2 and MnO2 as active materials,and active carbon as basic materials.
以提高超级电容器电极材料的电化学性能为目的,在活性碳粉末中掺入二氧化钌和二氧化锰,作为电极材料的活性物质,从而制备氧化物/活性炭多元复合电极,组装成超级电容器单元。
补充资料：超细二氧化钌粉末
分子式：
CAS号：
性质：微米级粒度的二氧化钌粉末，球状或树枝状。摇实密度1.25～1.5g/cm3。平均粒度<1.0μm，比表面积40～60m2/g。将纯金属钌转入溶液生成一定浓度的氯钌酸，加碱中和生成氢氧化钉、洗涤、烘干、磨细和脱水而成。用作厚膜电阻浆料的导电相。
CAS号：
性质：微米级粒度的二氧化钌粉末，球状或树枝状。摇实密度1.25～1.5g/cm3。平均粒度<1.0μm，比表面积40～60m2/g。将纯金属钌转入溶液生成一定浓度的氯钌酸，加碱中和生成氢氧化钉、洗涤、烘干、磨细和脱水而成。用作厚膜电阻浆料的导电相。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。