1) antiwear silicon fume concrete
抗磨蚀硅粉混凝土
2) abrasion of concrete
混凝土磨蚀
3) siliceous concrete
硅粉混凝土
1.
The reservoir has safely operated for12years since C 60 siliceous concrete used to line water release tunnel in1991and the abrasion in the base of tunnel has become decreased.
三屯河水库全年放水量中含沙量较大,水库放水隧洞在挟沙高速水流作用下,底部磨蚀严重,在采用几种材料衬护后都无法达到设计与安全运行,1991年采用C60硅粉混凝土对放水隧洞进行衬护,通过12a的运行,隧洞底部磨蚀量较小,运行可靠,达到设计要求,给水库安全防洪、排砂运行,保证灌溉带来了良好的经济效益。
4) silicon powder concrete
硅粉混凝土
1.
Application of shrinkage-compensating silicon powder concrete to Baishan Hydropower Station;
补偿收缩硅粉混凝土在白山水电站的应用
2.
Discussion on principle and requirement of choice of high-speed flow protecting surface material of silicon powder concrete;
由硅粉混凝土应用中存在的问题论高速水流护面材料选择的原则与要求
3.
Application of silicon powder concrete for flood discharge middle outlet in the Baojixia Reservoir Project;
硅粉混凝土在宝鸡峡水库泄洪中孔的应用
5) silica fume concrete
硅粉混凝土
1.
The use of silica fume concrete can effectively improve the impermeability of concrete,frost resistance,Anti-abrasion and anti-corrosive.
北方水工混凝土普遍存在着混凝土冻融剥蚀问题,采用硅粉混凝土能有效提高混凝土的抗渗性、抗冻性、抗冲磨性和抗侵蚀性,无毒便于施工,成本较低,是大面积混凝土剥蚀破坏表面的首选修补材料。
2.
Combining with concrete project example,the author studies the preparation of silica fume concrete and silica fume fly ash concrete based on experiment,and analyzes and compares their economy,gets the conclusion that the silica fume fly ash concrete has higher collapsed slump than silica fume concrete,and has better project economy and applicability.
结合具体的工程实例,通过试验对硅粉混凝土和硅粉粉煤灰混凝土的制备进行了研究,并对二者的经济性作了分析比较,得出硅粉粉煤灰混凝土较硅粉混凝土的坍落度高,且工程经济性与适用性强的结论。
6) abrasion concrete
磨蚀性混凝土
补充资料:硅质耐火混凝土
分子式:
CAS号:
性质:以硅石和废旧硅砖作为耐火骨料制成的耐火混凝土。其荷重软化温度接近于耐火度,传热性能好,抗酸性侵蚀能力强。制作时还加入胶结剂如水玻璃、磷酸盐、硫酸盐等。主要用在钢铁冶炼的焦炉、高炉、热风炉和均热炉等工业窑炉。
CAS号:
性质:以硅石和废旧硅砖作为耐火骨料制成的耐火混凝土。其荷重软化温度接近于耐火度,传热性能好,抗酸性侵蚀能力强。制作时还加入胶结剂如水玻璃、磷酸盐、硫酸盐等。主要用在钢铁冶炼的焦炉、高炉、热风炉和均热炉等工业窑炉。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。