1) preparation of solar-grade silicon
太阳级硅制备技术
2) Solar grade silicon
太阳级硅
1.
It is necessary to research and develop a production process for solar grade silicon, which is of low cost and independent of electronic industry, in order to meet rapid market demand of solar cells in the world.
随着光伏产业的迅速发展,太阳级硅原料供给不足已经成为光伏产业发展的最主要的瓶颈之一。
2.
A lot of researches show that the efficiency can reach 80% of single crystal silicon, by using solar grade silicon with purity of 4N to 6N for solar cell fabrication,but the cost only a quarter of that.
大量研究表明,使用纯度为4N～6N的太阳级硅制备太阳电池,效率可以达到单晶电池的80%,但是成本只有其四分之一。
3) solar-grade Silicon
太阳级硅
1.
Hence,it is technologically feasible for the production of low-cost solar-grade Silicon material.
处理后的硅粉还可进行熔化—固化—粉碎再处理,因此这是一种技术上可行的太阳级硅制备新方法。
2.
This thesis for master degree contains the experimental and theoretical research for the preparation technology of cheap solar-grade silicon.
本学位论文围绕等离子体制备太阳级硅的技术开展了一系列研究工作。
3.
The research for preparation of solar-grade silicon has become a hot research area in different countries.
最近光伏产业发展迅速,对太阳级硅的需求急剧增长,制备太阳级硅的技术成为现在各国的一个研究热点。
4) technology and equipment of manufacturing aluminium water heater solar energy
铝制太阳能热水器制造技术与设备
5) Solar grade silicon
太阳能级硅
1.
More and more attentions have been paid to the research of producing solar grade silicon by refining metallurgical grade silicon.
随着光伏市场需求不断增加,满足光伏电池技术经济指标要求的硅材料出现严重短缺,低成本提纯冶金硅至太阳能级硅工艺技术越来越受到广泛重视,成为研究开发热点。
2.
A new way using optical fiber wastes as raw material for the preparation of electrolytic reduction of solid SiO2 to Si in molten chlorides was proposed to be a considerable technology to prepare solar grade silicon (SOG-Si).
提出了以废弃石英光纤为原料,利用熔盐直接电解还原SiO2来制备太阳能级硅的新思路设计,该设计具有低成本低能耗、环保、工艺流程简单以及产品纯度高等优点。
3.
In order to prepare solar grade silicon(SOG-Si) by removing impurities from metallurgical grade silicon(MG-Si),basing on the difference of aluminum solubility in the solid phase and the liquid phase during the solidification of MG-Si,the impurity aluminum is removed from MG-Si by directional solidification in this paper.
为了去除工业硅中的杂质制备太阳能级硅,根据工业硅凝固过程中铝在固相和液相中溶解度的差异,采用定向凝固法去除工业硅中的杂质铝。
6) solar grade silicon solar cell
太阳级硅太阳电池
补充资料：硅多晶的硅烷法制备
硅多晶的硅烷法制备
polycrystalline silicon manufacture by silane process
gUIdUOJIng de gu一Wanfa zh一bei硅多晶的硅烷法制备(polyerystalline silieonmanufaeture by silane proeess)以甲硅烷作.介质的硅材料超提纯技术。是硅多晶的重要生产方法之一。其实质是先用硅粉或硅的化合物制成甲硅烷(SIH小然后用精馏等方法进行提纯，将纯SIH4经热分解siH;干里止篷些生51+2H2而得硅多晶。siH、无腐蚀性，热分解温度低且分解率高，故此法所得硅多晶的纯度高，产率高;但因SIH魂易燃易爆，需采取专门措施。 2。世纪50年代，一些厂家曾试图用硅烷法制造硅多晶，均因未解决好爆炸问题而被迫停产。首先实行稳定生产的是日本小松电子金属公司与石嫁研究所合作开发的以硅化镁作原料的工艺。其反应式为: NH。 MgZSi+4NH;CI一SIH4个斗ZMgC12+4NH:个 siH。再经低温精馏，然后经热分解得硅多晶棒。由于合成过程中有NH3存在，在以下工序的设备上装有真空夹套，较彻底地解决了燃烧与爆炸问题。此法于1960年开始生产，硅多晶的纯度优于西门子法(见硅多晶的西门子法制备)，其硼含量一般小于千亿分之一。但由于成本高等原因，其生产规模停滞在很小的水平上。 美国联合碳化物(UCC)公司研究成功了新硅烷法，使成本大幅度降低，并于1985年正式投产。此法利用如下合成和歧化反应获得硅烷: 51+2H2+3SICI;一4SIHC13 65爪HC13一3SIHZC12十3SICI咋 4SIHZC12一ZSIH3CI+ZSIHC13 3SIH3CI一SIHZCI:+SIH、 整个过程是闭路，一方投入硅与氢，另一方获得硅烷，因此排出物少，对生态环境有利，同时材料的利用率高。硅多晶的纯度高，其硼含量同样小于千亿分之一。产品多用于制备区熔硅单晶，包括辐射探测器用硅单晶(见辐射探测器用锗单晶和辐射探刚器用硅单晶)，也用于优质直拉硅单晶(见半导体硅材料)的制备。 美国埃西尔(Ethyl)公司利用磷肥生产的副产品制成硅烷，经提纯后进入流态化床进行热分解，制成平均粒径为0.7~。.75mm的颗粒状硅多晶，其硼含量小于0.3ppba，已批量生产。这种产品已用于硅的直拉法单晶生长，有可能用于正在开发的连续直拉法单晶生长。 (万群)