1) ZnO whiskers and particles
ZnO晶须及颗粒
2) SiCw/SiCp
SiC晶须/颗粒
1.
The new TN30W cutting tools of cermet composites were fabricated with the vacuum sintering technique while the SiCw/SiCp are added to the TN30 cutting tools.
在TN30金属陶瓷切削刀片中添加SiC晶须/颗粒,采用真空烧结法制备出新型TN30W金属陶瓷复合材料刀具。
3) T-ZnO whisker
T-ZnO晶须
1.
Tetrapod-shaped zinc oxide(T-ZnO) whiskers were prepared by the method of vapor phase oxidation at high temperature with bentonite as catalyst,and the influence of experimental conditions to T-ZnO whiskers were discussed in this article.
结果表明:实验温度、催化剂含量和空气流量对T-ZnO晶须的尺寸、规整性、产率等有显著的影响,实验温度为920~980℃,膨润土含量为33%左右以及适当的空气流量条件下,可以得到尺寸均一、结构规整、四脚状含量和晶须产率都较高的T-ZnO晶须。
2.
Nickel coatings were prepared on the surface of T-ZnO whiskers by electroless plating technique.
采用XRD,SEM及EDS对化学镀镍后的T-ZnO晶须进行了结构、形貌以及成分表征。
4) ZnO whiskers
ZnO晶须
1.
The growth mechanisms are investigated for the two ZnO whiskers with differentmorphology.
以Zn粉为原料,采用气固反应方法制备出两种一维ZnO晶须:ZnO纳米线和ZnO短晶须。
5) ZnO whisker
ZnO晶须
1.
ZnO whisker,the only tetrapod-shaped whisker among all kinds of whiskers, possesses good com prehensive properties such as somieonductivity, wear resistance, vibration insulation and microwave absorption, taking advantage of its peculiar shape and single crystalline character.
ZnO晶须是一种立体四针状单晶体微纤维,具有多功能特性。
2.
The different morphologies of high-quality ZnO whisker materials have been synthesized by thermal evaporation methods,which include wires,rods,and multiple morphologies.
采用热蒸发法制备出高纯度线状、棒状、多脚状的不同形态ZnO晶须材料。
6) T-ZnO whiskers
T-ZnO晶须
1.
The micro morphology, crystal structure, electric conducting properties, optical properties and moisture sensitive characteristics of as-doped T-ZnO whiskers were measured and analyzed.
本论文对四针状ZnO(T-ZnO)晶须进行了本征缺陷的控制以及非本征缺陷的掺杂,并对掺杂后的T-ZnO晶须的晶体结构、微观形貌、电学性能、光学性以及湿敏特性进行了表征和研究。
补充资料：多晶莫来石晶须(纤维)
分子式：
CAS号：
性质：莫来石相为主晶相的多晶纤维。化学成分为Al2O3 72％～77％，SiO222％～17％，B2O3 3％～5％，P2O51.5％～3.0％。纤维直径2～7μm，纤维长度20～125μm。使用温度1350℃。多采用溶胶-凝胶法制造。主要用作补强填料，也可作为轻质、隔热保温材料使用。
CAS号：
性质：莫来石相为主晶相的多晶纤维。化学成分为Al2O3 72％～77％，SiO222％～17％，B2O3 3％～5％，P2O51.5％～3.0％。纤维直径2～7μm，纤维长度20～125μm。使用温度1350℃。多采用溶胶-凝胶法制造。主要用作补强填料，也可作为轻质、隔热保温材料使用。