3) square crystalloid
四方相
1.
The quality of the sol-gel system was enhanced,and the square crystalloid nanometer barium titanate powder was gained after being calcined at 700℃ by the improved c.
根据胶体的形成机理和条件,对目前的研究工艺进行优化,制备过程中不引入H+和NO3-,在提高胶体稳定性的基础上,于700℃左右煅烧获得了各向同性、粒径约20nm的四方相Ba-TiO3粉体,解决了普遍存在的BaTiO3粉体粒径细小与四方相的矛盾,煅烧温度也较常规方法明显降低。
2.
Square crystalloid nano-size barium titanate powders were prepared by an improved oxalate coprecipitation method,since the phase would go far away the square crystalloid when the powders size was reduced by traditional technics.
根据传统的草酸盐共沉淀法合成超细BaTiO3粉末易产生偏离四方相的特点,提出了一种改进的草酸盐共沉淀法制备BaTiO3粉体的方法。
4) tetragonal
[英][te'trægənəl] [美][tɛ'trægənḷ]
四方相
1.
Hydrothermal synthesis of tetragonal barium titanate from barium chloride and titanium tetrachloride;
水热合成高纯四方相钛酸钡纳米粉末研究
2.
Sintered sample which has different amount of monoclinic and tetragonal phase at room temperature is obtained at different sintering temperature.
通过化学组成和相含量设计,采用湿混法制备了MgO和Y2O3共同稳定ZrO2粉末,在不同的温度下烧结,获得了室温下单斜相和四方相含量不同的烧结样品,用X射线峰宽化法测定并计算了粒子尺寸。
3.
The pattern of XRD illustrated that the pure perovskite phase (tetragonal) had been obtained for all samples.
XRD分析结果表明所制备的样品都生成了纯的钙钛矿结构,并且都为四方相。
5) ZrO 2 tetragonal phase
ZrO2四方相
6) tetragonal phase BaTiO 3
四方相BaTiO3
补充资料：三种发相──嗔恚三种发相
【三种发相──嗔恚三种发相】
﹝出释禅波罗蜜次第法门﹞
［一、非理嗔相］，谓行人修禅定时，嗔觉欻然而起，无问是理非理，他犯不犯；无故而发嗔恚，障诸禅定，是为非理嗔相。
［二、顺理嗔相］，谓行人修禅定时，外人实来恼我，以此为缘，生于嗔觉，相续不息；亦如持戒之人，见非法者，而生嗔恚。嗔虽顺理，亦障禅定，是为顺理嗔相。
［三、诤论嗔相］，谓行人修禅定时，着己所解之法为是，谓他所行所说悉以为非。外人所说不顺己情，即恼觉心生，而起嗔恨，障诸禅定，是为诤论嗔相。
﹝出释禅波罗蜜次第法门﹞
［一、非理嗔相］，谓行人修禅定时，嗔觉欻然而起，无问是理非理，他犯不犯；无故而发嗔恚，障诸禅定，是为非理嗔相。
［二、顺理嗔相］，谓行人修禅定时，外人实来恼我，以此为缘，生于嗔觉，相续不息；亦如持戒之人，见非法者，而生嗔恚。嗔虽顺理，亦障禅定，是为顺理嗔相。
［三、诤论嗔相］，谓行人修禅定时，着己所解之法为是，谓他所行所说悉以为非。外人所说不顺己情，即恼觉心生，而起嗔恨，障诸禅定，是为诤论嗔相。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条