1) C_f/SiC ceramic matrix composites
C_f/SiC陶瓷基复合材料
2) 2D C_f/SiC composites
2D C_f/SiC复合材料
1.
The tensile properties of the 2D C_f/SiC composites were characterized by uniaxial tensile tests,and the tensile strength, modulus and fracture strain of the composites were 181.
研究了先驱体转化2D C_f/SiC复合材料的拉伸行为。
3) Cf/SiC composites
C_f/SiC复合材料
1.
The oxidation-resistance coatings of the Cf/SiC composites by spraying processing were investigated in this paper.
研究了涂刷法制备C_f/SiC复合材料抗氧化涂层,重点讨论胶粘剂体系组成对涂层性能的影响。
4) 2D-Cf/SiC composite
2D-C_f/SiC复合材料
6) Cf/SiC composite
Cf/SiC陶瓷基复合材料
1.
Using the mixed powder of Cu,Ti and graphite Cf/SiC composite was brazed to Ti alloy under vacuum condition.
研究用Cu粉、Ti粉、石墨粉组成的混合粉末真空钎焊Cf/SiC陶瓷基复合材料和钛合金,采用X射线衍射、扫描电镜和能谱仪对接头组织结构进行分析。
2.
Using the mixed powders of Cu,Ti and graphite,Cf/SiC composite was brazed to Ti-6Al-4V alloy under vacuum condition.
用Cu粉、Ti粉、石墨粉组成的混合粉末连接Cf/SiC陶瓷基复合材料和TC4钛合金,采用X射线衍射、扫描电镜和能谱仪对接头组织结构进行分析。
补充资料：陶瓷基复合材料
分子式：
CAS号：
性质：ceramic matrix composite 以陶瓷材料为基体，并以陶瓷、碳纤维和难熔金属的纤维、晶须、晶片和颗粒为增强体，通过适当的复合工艺所构成的复合材料。陶瓷基复合材料主要为改善原陶瓷基体材料的本征脆性，避免突发性破坏，提高其工程可靠性。常用的陶瓷基体有氧化物(如氧化锆和氧化铅)、碳化物(如碳化硅)、氮化物(如氮化硅)等。陶瓷基复合材料由于加入增强体后对其韧性有明显改善，如碳纤维增强硅-铝-氧-氮(sialon)陶瓷的断裂韧性由原基体的2.2MPa·ml/2提高到9.5MPa·ml/2，但其抗弯强度仍维持298MPa。由于陶瓷基复合材料发展历史短，在工艺过程中容易发生界面反应使增强体退化，工艺方法不成熟，尚在研究开发阶段。
CAS号：
性质：ceramic matrix composite 以陶瓷材料为基体，并以陶瓷、碳纤维和难熔金属的纤维、晶须、晶片和颗粒为增强体，通过适当的复合工艺所构成的复合材料。陶瓷基复合材料主要为改善原陶瓷基体材料的本征脆性，避免突发性破坏，提高其工程可靠性。常用的陶瓷基体有氧化物(如氧化锆和氧化铅)、碳化物(如碳化硅)、氮化物(如氮化硅)等。陶瓷基复合材料由于加入增强体后对其韧性有明显改善，如碳纤维增强硅-铝-氧-氮(sialon)陶瓷的断裂韧性由原基体的2.2MPa·ml/2提高到9.5MPa·ml/2，但其抗弯强度仍维持298MPa。由于陶瓷基复合材料发展历史短，在工艺过程中容易发生界面反应使增强体退化，工艺方法不成熟，尚在研究开发阶段。