1) sintering conditions
烧结制度
1.
It shows that the ferrite core must contain proper Fe 2+ content by accurately controlling the sintering conditions such as sintering temperature and atmosphere,and reducing the Zn evaporation from the ferrite cores.
通过对烧结制度如温度、气氛曲线实行精确控制，使铁氧体中保持适当的Ｆｅ２＋含量，同时尽量减少铁氧体中Ｚｎ的挥发，这是获得高磁导率ＭｎＺｎ铁氧体的重要保证。
2.
The ferrite powders were pressed into toroidal shapes and then sintered under different sintering conditions with different contents of additive.
为了确定自蔓延高温合成(SHS)NiFe2O4的最佳烧结制度,通过SHS技术制备获得NiFe2O4粉末,加入不同含量的添加剂Bi2O3,在不同烧结温度和保温时间下进行烧结。
2) Sintering Temperature
烧结温度
1.
Effects of sintering temperature on fatigue damage of alumina ceramics;
烧结温度对氧化铝陶瓷疲劳损伤过程的影响
2.
Effect of sintering temperature on contexture and performance of iron-based P/M aircraft brake materials;
烧结温度对铁基粉末冶金航空刹车材料组织的影响
3.
Effect of sintering temperature on microstructure and mechanical property of ceramic corundum abrasives;
烧结温度对陶瓷刚玉磨料性能的影响
3) sintered density
烧结密度
1.
Effects of process parameters on the gelcasting green strength and sintered density of stainless steel;
工艺参数对凝胶注模成型不锈钢坯体强度和烧结密度的影响
2.
The influence of Cr on sintered density, microstructure and wear resistance of FeNiMo system prealloyed powders were investigated.
研究了铬对Fe-Ni-Mo系粉末烧结密度、微观组织特征及耐磨性能的影响,通过SEM观察分析了磨损形貌,探讨了其摩擦磨损机制。
3.
It is found that the green density and sintered density of YBa_2Cu_3O_(7-δ) powders with different granularity varied differently with the variation of pressure.
结果表明,不同粒度YBaCuO超导粉体的压坯密度、烧结密度(即烧结前后的致密度)随压力的变化规律不同。
4) Sinter temperature
烧结温度
1.
07%the sinter temperature of magnet reaches 1110 ℃with no abnormal grain growth and coercivity reaches 1021 kA/m and the addition of Nb benefits the squareness of magnet;When the addition of Nb and Zr both reach 0.
07%,磁体烧结温度可达到1110 C,晶粒不发生异常长大,矫顽力达到1021kA/m,Nb的添加对提高磁体的方形度有利。
2.
The microcosmic structure and radiant performance of transition metal oxides radiant powder basic material with main component of Fe_2O_3 under different sinter temperature were introduced.
本文介绍了不同温度下烧结的以 Fe_2O_3为主要成分的过渡金属氧化物辐射材料的微观结构与辐射性能,分析了烧结温度对其矿物组成、微观结构及辐射性能的影响关系,探讨了改善 Fe_2O_3基辐射材料红外辐射性能的掺杂方式。
3.
07at%, the sinter temperature of magnet could reach to 1110 ℃ with no abnormal grain growth, and coercivity increased to 1021 kA/m.
07%,磁体的烧结温度可高达1110℃,晶粒不发生异常长大,矫顽力达到1021kA/m左右,Nb的添加提高了磁体的方形度。
5) gradient sintering
梯度烧结
6) sintering rate
烧结速度
1.
The sintering process of compacts of nanocrystalline Cu powder by spark plasma sintering (SPS) was investigated with emphasis on the effects of the temperature and sintering rate on grain size, relative density and electrical resistances of the samples by SPS.
利用放电等离子烧结装置考察了纳米铜粉坯体的升温过程,研究了烧结速度和烧结温度对烧结等效电阻、烧结体相对密度及晶粒尺寸的影响。
补充资料：带式烧结机烧结
带式烧结机烧结
sintering by sinter strand
一种应用最广的铁矿石烧结方法。带式烧结机是钢铁工业的主要烧结设备，它的产量占世界烧结矿的”%。现代带式烧结机的烧结室的断面示于图1。烧结机是由铺设在钢结构上的封闭轨道和在轨道上连续运动的一系列烧结台车组成。首先将从烧结矿中分出的铺底料(10~Zomm)加在台车上，以保护台车算条和减少废气含灰量。然后再将烧结混合料经布料机加到台车上，并保持规定的高度。随之进行抽风点火烧结，随台车前进，烧结过程由料层表面不断向下进行。至机尾，烧结完成，台车翻转将烧结饼倾卸。空台车沿下部轨道运行至烧结机头部，再加料进行点火烧结，如此循环不断。烧结饼经破碎和筛出热返矿后，送冷却机冷却。从料层中抽出的废气经台车下的风箱至集气总管和除尘装置，由抽风机排向烟囱。dalshi shaojieji shaojie带式烧结机烧结(sintering by sinter strand)}馨爵鬓 森币乒、，一，，，，.、一，r，_， 图1现代抽风带式烧结机烧结室断面图 带式烧结机由烧结台车、密封装置、钢结构框架和3.om、3.sm、4.om及5.om几种。由于台车处于高温传动装置组成。台车是放置烧结料和进行抽风烧结的下工作，因之不仅要求材质能耐高温、而且要求结构合重要部件。它是由铸钢车体、侧板、算条和滚轮组成(见理减少高温变形的影响。在台车和风箱滑道之间有密图2)。按烧结机大小、台车宽度有1.sm、2.om、2.sm、封装置(水管式密封或弹簧式密封)，对减少漏风和节 省电耗有很重要的作用。在机头和机尾的风箱隔板与 ‘卜~一一-一-2500—--，司 创盯一一一下台车之间用重锤连杆式密封。为保证台车在受热膨胀 .对胭奎至斋荞至幕筹拜三三三三三尸气润后仍能平稳运转，在机尾卸矿端设置专门的摆动机架 书阳~一一一即一一邵一二一一一.一-期d{丹一去或可水平移动的尾部星轮。烧结台车借助于机头部分 !毛一一一一，。。州泞的传动装置向前运动，传动装置是由电动机、减速机和 卜卜一一一一-—3216—一一一一月’传动大齿轮所组成。(见彩图插页第2、3页) (杨兆祥蔡法率)纂戳磷~ 图2烧结台车