1) low-temperature electrolytic sulphurization
低温电解渗硫
2) low temperature liquid sulphurizing
低温渗硫
3) electrolgtic sulphurizing
电解渗硫
5) low temperature ion sulphurization
低温离子渗硫
1.
Sulphurized layer was produced on the surface of CrMoCu alloy cast iron by means of low temperature ion sulphurization process with thickness of about 5 μm.
采用低温离子渗硫技术在CrMoCu合金铸铁表面形成厚度约5μm渗硫层,渗硫层表面分布均匀,其相组成主要为FeS。
2.
Sulfide layers were made on the surface of AISI 1045 and SAE 52100 steels by means of low temperature ion sulphurization process.
采用低温离子渗硫技术在４５＃ 钢和ＧＣｒ１５ 钢表面形成渗硫层，用ＳＲＶ 往复摩擦磨损试验机分别在干摩擦和液体石蜡润滑下对渗硫层的摩擦学性能进行了研究，用ＳＥＭ、ＥＤＡＸ 和ＸＲＤ研究了渗硫层的形貌和结构，并对磨痕的形貌及成分进行了分析。
3.
After carbonization and heat treatment for the carbonized bearing steel G20CrNi2Mo applied for the rolling bearings on railway cars, the processing of low temperature ion sulphurization is made.
对铁路车辆滚动轴承使用的渗碳轴承钢G20CrNi2Mo经渗碳和热处理后,进行了低温离子渗硫处理。
6) low temperature ion sulfuration
低温离子渗硫
1.
The composite solid lubrication sulfuration layer between metal molybdenum and solid lubricant molybdenum disulfide (MoS2) was obtained after the metal molybdenum layer with 3 μm thick was treated by low temperature ion sulfuration.
对厚约3μm的金属钼薄膜进行低温离子渗硫处理,得到了单质金属钼与固体润滑剂二硫化钼(MoS2)共存的复合固体润滑渗硫层。
2.
Solid lubrication FeS films were prepared on non-ferrous metal (Si) surface by two-step method, namely composite processing between radio-frequency sputtering Fe and low temperature ion sulfuration.
通过两步法,即射频溅射Fe膜与低温离子渗硫复合处理工艺,在非黑色金属(单晶硅)表面得到了固体润滑FeS薄膜。
补充资料：低温离子渗硫
低温离子渗硫
精密离子均匀轰击
1、低温离子渗硫
在 20 世纪八十年代，材料物理学家张弋飞在世界上首先发现，固体硫蒸气产生辉光放电的效应，该效应使金属零件在低温下形成固体润滑层—渗硫层。 这就是著名的“低温离子渗硫”，它的全称是金属表面形成硫化物层的方法和设备，获得了 中、英、德、法、瑞、意、日等多国专利。
至1997年底，低温离子渗硫专利普通许可21家企业生产，取得广泛的经济效益和社会效益。
国内一些企业和科研单位声称开发出“离子渗硫”、“离子硫化”、“真空等离子渗硫”，或称“国外引进”；三家企业被北京市中院判决侵权，一家被宣告实用新型专利无效；见侵权维权
实际上，离子渗硫只有一个能达到120微米渗层深度发明专利，，即“金属表面形成硫化物层的方法和设备”专利。