1) layer/additive forming
分层/堆积成形
2) Material deposition
堆积成形
4) SMDS
分段堆积/雕铣成形
1.
Design of Automatic Extrusion Device for Sacrificial Support Material of Segmented Manufacturing Using Deposition and Sculpture(SMDS);
分段堆积/雕铣成形支撑材料自动挤出装置设计
5) overlaying shaping
堆焊层成形
1.
The influence of overlaying technology on the performance of FeAl intermetallic compound overlaying shaping was studied by orthogonal experiment,the extent of influence on the performance of overlaying shaping was evaluated through the range analysis and variance analysis,and the technologic parameters of the overlaying technology were optimized.
采用正交试验法研究了堆焊工艺对FeA l金属间化合物堆焊层成形质量的影响,通过极差分析和方差分析,评价了堆焊工艺参数对成形质量影响的显著程度,并对堆焊工艺参数进行了优化。
6) fused deposition modeling(FDM)
熔融堆积成形
1.
This article analyzed the change rules of bonding temperature of extruded fibers with deposition time and deposition path in the process of fused deposition modeling(FDM).
分析了熔融堆积成形(FDM)工艺中挤出丝材的温度随时间、路径的变化规律,通过对丝材物理模型的合理假设,建立了挤出丝材温度场的数学模型,并根据Stratasys商用机FDM2000所使用的ABS-P400丝材的热学参数,结合聚合物的粘结机理,验证了模型的合理性。
补充资料：主要射出成形材料成形时应注意事项
■主要射出成形材料成形时应注意事项
品 名 注 意 事 项
PVC
聚氯乙烯
1. 产品种类范围非常广（硬质、软质、聚合物等），成型条件各有不同，从熔融至分
解之温度范围很小，尤须注意加热温度。
2. 附着水分少，但成型周期尽可能减少（50℃~60℃热风干燥）。
3. 成型机方面，与材料直接接触的部位须电镀或采用不锈钢以防热分解所产生的盐酸
侵蚀。射出压力2100kg/cm2程度。
4. 所有塑料当中必须是细心注意温度调节。
5. 浇口附近易产生流纹，故射出操作后，柱塞不要后退使浇口充分固化后再瞬间退后为宜。
6. 加热之初温不宜高，特别注意熔融情形。第二级加热温度较高，且尽可能使成形周
期缩短，比较安全。
PA
聚醯胺树脂
1. 成型温度比其它材料高，故采用油加热的成形机较适当。
2. 吸湿性大，必须充分干燥。水分对成型品的品质影响甚大（80℃热风干燥约5~6小时）。
3. 须退火以消除内部歪斜。
PP
聚丙烯
1. 同PE，但成形温度必须较高。熔融温度170℃，超过190℃则流动性大增，则毛边增加，
易产生接缝及凹入情形。
PC
聚碳酸脂
1. 吸湿性比尼龙小，但若有些微之水分存在则成型品产生其它色泽或气泡，故必须密封
干燥同时成形时也须预备干燥（120℃之温度4小时）。
2. 加热温度超过320℃时则产生热分解，成品变色，故特别注意温度调节，又成型时的温度调节也非常重要，须特别注意其最低温度、最低时间。
3. 须退火以消除内部歪斜（130℃~135℃，1小时程度为准）。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。