说明:双击或选中下面任意单词,将显示该词的音标、读音、翻译等;选中中文或多个词,将显示翻译。
您的位置:首页 -> 词典 -> 地下钢质煤气储罐
1)  Underground steel gas holder
地下钢质煤气储罐
2)  underground steel storage tank
地下钢质储罐
1.
In order to guarantee the long time and safe operation of the underground steel storage tanks,the most economic and effective anticorrosive method for newly built storage tanks is to add cathodic protection on the cover layer.
分析了地下钢质储罐的腐蚀原因 ,提出了新建储罐腐蚀控制应采用的措施 ,重点介绍了阴极保护的几个主要问
3)  underground gas-holder
地下储气罐
4)  gas container
煤气储罐
1.
The diffusion model and its simulation ofthe leakage from gas containers;
煤气储罐泄漏扩散模型及仿真
5)  underground tank
地下储罐
1.
Evaluation of source intensity of underground tank explosion accident;
地下储罐爆炸事故源强估算
6)  Underground Storage Tank
地下储罐
1.
The underground storage tank and its piping of oil products used more and more often in the selling and storage course.
石油类产品的地下储罐及其管道系统正在越来越多的应用到销售、储备等领域,但是随着其数量的增多,人们发现这套地下系统会对生态环境造成不可忽略的污染。
补充资料:45钢和40Cr钢调质的热处理工艺
45钢40Cr钢调质                         
    调质是淬火加高温回火的双重热处理,其目的是使工件具有良好的综合机械性能。
    调质钢有碳素调质钢和合金调质钢二大类,不管是碳钢还是合金钢,其含碳量控制比较严格。如果含碳量过高,调质后工件的强度虽高,但韧性不够,如含碳量过低,韧性提高而强度不足。为使调质件得到好的综合性能,一般含碳量控制在0.30~0.50%。

    调质淬火时,要求工件整个截面淬透,使工件得到以细针状淬火马氏体为主的显微组织。通过高温回火,得到以均匀回火索氏体为主的显微组织。小型工厂不可能每炉搞金相分析,一般只作硬度测试,这就是说,淬火后的硬度必须达到该材料的淬火硬度,回火后硬度按图要求来检查。 

工件调质处理的操作,必须严格按工艺文件执行,我们只是对操作过程中如何实施工艺提些看法。


   1、 45钢的调质
   45钢是中碳结构钢,冷热加工性能都不错,机械性能较好,且价格低、来源广,所以应用广泛。它的最大弱点是淬透性低,截面尺寸大和要求比较高的工件不宜采用。


   45钢淬火温度在A3+(30~50) ℃,在实际操作中,一般是取上限的。偏高的淬火温度可以使工件加热速度加快,表面氧化减少,且能提高工效。为使工件的奥氏体均匀化,就需要足够的保温时间。如果实际装炉量大,就需适当延长保温时间。不然,可能会出现因加热不均匀造成硬度不足的现象。但保温时间过长,也会也出现晶粒粗大,氧化脱碳严重的弊病,影响淬火质量。我们认为,如装炉量大于工艺文件的规定,加热保温时间需延长1/5。


   因为45钢淬透性低,故应采用冷却速度大的10%盐水溶液。工件入水后,应该淬透,但不是冷透,如果工件在盐水中冷透,就有可能使工件开裂,这是因为当工件冷却到180℃左右时,奥氏体迅速转变为马氏体造成过大的组织应力所致。因此,当淬火工件快冷到该温度区域,就应采取缓冷的方法。由于出水温度难以掌握,须凭经验操作,当水中的工件抖动停止,即可出水空冷(如能油冷更好)。另外,工件入水宜动不宜静,应按照工件的几何形状,作规则运动。静止的冷却介质加上静止的工件,导致硬度不均匀,应力不均匀而使工件变形大,甚至开裂。


说明:补充资料仅用于学习参考,请勿用于其它任何用途。