1)  wear-resistant technique
耐磨技术
1.
The paper analyzes the existing wear-resistant techniques in the cyclone collector and presents an active wear-resistant technique that is new and unique,which prolongs service life of the cyclone collector 5～10 times, benefits to the reliability and practicality of it testified by experiment.
分析了旋风除尘器现用耐磨措施,提出了在旋风除尘器易磨部位设置料盒来抵抗磨损的新型耐磨技术通过现场试验研究证实,它可提高旋风除尘器的性能,并使其使用寿命延长5～10倍,具有良好的社会、经济效益图3,表3,参
2)  wear-resistant
耐磨
1.
Application of wear-resistant and lubricating coating for wood cutting tools;
润滑耐磨功能涂料在木工刀具上的应用
2.
The wear-resistant material with best composition and overlay welding process were successfully developed,and the productiviting and the economic benefit were obviously improved.
通过对碎煤齿环的失效分析 ,找出了影响齿环寿命的因素及薄弱环节 ,并研制成功了最优成分的耐磨材料和堆焊工艺 ,显著提高了生产率和企业的经济效
3)  wear-resistance
耐磨
1.
Application on new nitriding coating technology of tube's corrosion-resistanceand wear-resistance;
油管耐磨抗蚀氮化新工艺与应用
2.
Study of wear-resistance of chemical plating on the surface of 65Mn steel;
65Mn钢表面化学镀耐磨研究
3.
So we have to improve the wear-resistance of the rotor by hard anodic oxidation.
在纺纱过程中,转杯处于高速旋转状态,纤维的摩擦、负压气流的冲刷以及部分杂质的侵蚀和人为的清洁工作,均能造成转杯内壁和凝棉槽表面的磨损,因此为提高转杯的耐磨性须对其进行硬质阳极氧化处理。
4)  wear-resisting
耐磨
1.
Study on Oxide-alumine Porcelain of Low-temperature Wear-resisting Ueing High-alumina Clay;
利用高铝矾土研制低温耐磨氧化铝瓷
2.
Welding of wear-resisting steel Hardox400;
Hardox400耐磨钢的焊接
5)  abrasion resistance
耐磨
1.
Testing results showed that the coat was excellent in abrasion resistance, stain resistance and slip resistance.
结果表明涂层在耐磨、耐污和防滑性方面表现优异。
2.
Comparing with ordinary rubber sole, PU sole is light in weight with better abrasion resistance.
聚氨酯鞋底与普通橡胶鞋底相比,它具有质量轻、耐磨性能好等特点。
3.
In this article through the inspection of imported cyclone separators, the author discussed the examining methods of cyclones, analyzed the mechanics of abrasion resistance and cracking of the hard surfacing.
通过对进口旋风分离器的检验 ,探讨了旋风分离器的检验方法 ,对表面硬化层耐磨和开裂的机理进行了一些探讨 ,为了研究旋风分离器堆焊层表面裂纹的扩展情况 ,制作了裂纹对比试块 ,利用端点回波法测量了堆焊层裂纹自身高度 ,为利用超声波探伤仪测量裂纹深度提供了有效方
6)  wear resistance
耐磨
1.
Anti-friction and Wear Resistance Mechanism of FeS Layer;
FeS层的减摩耐磨机理
2.
The mechanism of wear resistance and reduction of metal ceramic coatings prepared by in-situ fabrication through laser cladding on the surface of oil well pump plunger;
激光合成金属陶瓷抽油泵柱塞耐磨减磨机理
3.
The thermal stability,thermal fatigue resistance,erosion resistance to aluminum liquid and thermal wear resistance of the new-developed high wear-resistant cast hot-working die steel were evaluated,their properties were compared with commercial H13 steel.
研制了一种高耐磨精铸热作模具钢,分析了其热稳定性、热疲劳性能、耐铝热熔损性能和热磨损性,并与H13钢进行了对比。
参考词条
补充资料：RP技术和基于RP技术的RT技术

摘要：介绍了快速成形技术的原理和几种典型成形方法。同时，还介绍了基于快速成形技术的快速模具技术在模具制造业中的应用，以及快速成形技术的现状和发展趋势。
    关键词：快速成形；快速模具；直接快速制模；间接快速制模。


引言
    快速成形（Rapid Prototyping , RP.）技术，也叫快速原型技术，20世纪80年代后期起源于美国。该技术是一种集计算机辅助设计、机械、数控、检测、激光技术和材料学等为一体的先进制造技术。传统的制造方法是基于材料去除的概念，而 RP 技术突破了这种工艺方法，它是一种“使材料生长”的制造过程，是一种全新的制造技术，所以被誉为是近20年来制造技术领域的一项重大突破。


RP技术
    1、原理
    RP 技术是基于离散/堆积的原理。在计算机的控制下快速成型机的成形头选择性地固化一层层的液体材料（或选择性的切割一层层的纸、烧结一层层的粉末材料、喷涂一层层的热熔性材料等），形成各个截面轮廓并逐步顺序叠加成三维工件实体。其工艺步骤为：
    （1）切片  把三维CAD模型转化为快速原型系统能够接受的数据格式，运用切片软件将模型切成一系列指定厚度的薄片。
    （2）扫描  通过数控装置控制激光或其他作业装置，在当前工作层上扫描出切片的截面形状。
    （3）进给  把工作台沿着某一方向下降每次成形厚度那样一个距离。重复上一步骤和本步骤，直到工件完全成形。
    （4）后处理  根据不同应用场合的需要，分别对零件进行后固化、上漆、烧结、渗铜等处理。
    2、类型
    目前RP的方法有几十种，但商品化较好的主要有：光固化立体成形（Stereo Lithogra- phy Apparatus, SLA）、分层实体制造（Laminated Objected Manufacturing ,LOM）、选择性激光烧结（Selected Laser Sintering , SLS）、熔融沉积造型（Fused Deposition Modeling , FDM）、三维印刷（Three Dimensional Printing , TDP）等。另外，很有潜力的激光气相沉积（Laser Vapor Deposition , LVP）法正在试验之中。
    （1）SLA  SLA法是出现最早，技术最成熟和应用最广泛的RP 技术，由美国的3D Systems 公司推出。SLA法是用激光束按照截面轮廓的形状，沿液态光敏树脂的表面进行扫描来固化光敏树脂，从而成形工件。工件的表面质量较好，尺寸精度较高（相对于其他RP 方法），可确保工件的尺寸精度在0.1mm以内，但树脂会因吸收空气中的水分而收缩、弯曲、卷翘，产生应力，适合成形中小型工件。

说明：补充资料仅用于学习参考，请勿用于其它任何用途。