1) high graphite transformation ratio
高石墨转化率
2) graphite transform
石墨转化率
1.
The graphite transform ratio of 70%, 80% and 90%, which is higher than the normal slice catalyst synthesis system has been achieved by powder catalyst.
通过实验， 实现了石墨转化率在７０％ 、８０ ％ 、９０ ％ 等较高水平的粉末触媒金刚石合成，并就此与片状触媒进行了对比分析；在此基础上，通过计算得出了粉状触媒和片状触媒合成金刚石的理论产量；这些结果有助于加强对粉末触媒应用潜力的认识。
3) graphitization degree
石墨化率
1.
The graphitization degree G is increased with the increment of the time and temperature.
结果表明，石墨化率与自焙时间和温度成正比。
2.
Thermal diffusivity, α, of self-baking carbon block with different graphitization degrees was determined experimentally by means of laser-pulse within temperature range of 200 1100℃.
采用激光脉冲加热及降温法测定了石墨化率不同的自焙炭块在２００—１１００℃范围内的热扩散率α。
5) graphitic globuring ratio
石墨球化率
1.
Thc graphitic rear ratio of single grain, mean value of graphitic area ratio and graphitic globuring ratio can be ealculated througy using of OMNICON 3600 image analyzer to determine graphitic roundness value and through using computer system to treat.
利用ＯＭＮＩＣＯＮ３６００图像分析仪测定石墨圆度值，通过计算机处理系统计算出单颗料石墨面积率、石墨面积率平均值和石墨球化率。
6) HP graphite electrodes
高功率石墨电极
1.
On the basis of these experiments a process for makin g HP graphite electrodes with mixed cokes as precursor was proposed.
分析了锦西焦与CGG油系针状焦的特性;以锦西焦为主加CGG油系针状焦为原料,生产Ф450mm高功率石墨电极,并对其生产过程中的工艺进行控制。
补充资料：临界转化率
分子式：
CAS号：
性质：在非线性逐步聚合反应中发生凝胶化时的转化率。其数值可以从理论计算得到。常用的方法有从改进的Carothers方程计算或从支化系数作统计考虑。两种方法得到的临界转化率并不相同，而一些实验测定的数值介乎这两种理论计算值之间。
CAS号：
性质：在非线性逐步聚合反应中发生凝胶化时的转化率。其数值可以从理论计算得到。常用的方法有从改进的Carothers方程计算或从支化系数作统计考虑。两种方法得到的临界转化率并不相同，而一些实验测定的数值介乎这两种理论计算值之间。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条