1) Brazilian disk specimen
巴西圆盘试样
1.
The mixed mode fracture of center cracked Brazilian disk specimen subjected to diametral compression is analysed by weight function method.
由于巴西圆盘试样可直接利用岩芯 ,而且可以通过改变裂纹与载荷线的夹角即可获得任意 K /K 比例的复合型加载 ,因此所提出的方法和结果对岩石断裂强度和复合型断裂准则的研究十分有
2) flattened Brazilian disk specimen
平台巴西圆盘试样
1.
The flattened Brazilian disk specimen is proposed to determine elastic modulusE,tensile strength ts and opening mode fracture toughness IcK for brittle rocks in one test simultaneously.
用平台巴西圆盘试样在一次试验中同时测定脆性岩石的弹性模量E、拉伸强度ts和张开型断裂韧度IcK。
3) flattened Brazilian disc specimen
平台巴西圆盘试样
1.
An experiment study on rock tensile strength with flattened Brazilian disc specimen under dynamic loading;
平台巴西圆盘试样岩石动态拉伸特性的试验研究
2.
The test method of the flattened Brazilian disc specimen is reviewed more comprehensively.
更全面地考察了用平台巴西圆盘试样的试验方法,该方法用一次实验估算岩石材料的3个力学参数,即弹性模量、拉伸强度和断裂韧度。
4) Brazilian disc test
巴西圆盘试验
1.
Brazilian disc test is an indirect experiment,proposed by International Society for Rock Mechanics,to determine the tensile strength of rock materials.
巴西圆盘试验是国际岩石力学学会推荐的用于测量岩石抗拉强度的间接实验,其理论基础是圆盘在荷载作用下应力场的分布。
5) Brazilian disc
巴西圆盘
1.
Brazilian disc is popular sample used for the measurement of tensile properties of brittle materials like marble.
巴西圆盘是用于测定大理岩等脆性材料拉伸性质的一种常用试样,为了研究温度对岩石在动态拉伸条件下破坏应变的影响规律,利用直径100 mm的分离式Hopkinson压杆对一系列大理岩巴西圆盘进行了动态劈裂试验,通过粘贴在试样中心处的应变片,得到了不同类型的试样在不同应变率下的破坏应变。
2.
The dynamic splitting tests of marble using Brazilian disc and flattened Brazilian disc were performed at high strain rate with split Hopkinson pressure bar(SHPB) of 100 mm diameter.
利用直径100 mm的分离式霍普金森压杆对大理岩巴西圆盘进行了动态劈裂试验。
3.
Flattened Brazilian disc samples were first chosen in the dynamic split tests.
首次把平台巴西圆盘试样引入动态劈裂试验。
6) Brazilian disk
巴西圆盘
1.
The finite element commercial code LS-DANA is used to study the deformation process of Brazilian disk with pre-existing crack under impact loading.
采用LS-DYNA有限元软件,对含中心裂纹的岩石巴西圆盘试件在冲击压缩荷载作用下的变形过程进行数值分析。
2.
The stress intensity factors, and of the Brazilian disks with variable angle and crack length are calculated by semi-analytical weight function method.
计算了不同裂纹长度和不同裂纹倾角的巴西圆盘的Ⅰ型和Ⅱ型应力强度因子,并将半解析权函数法计算结果与其它文献所提供的结果进行了比较,发现吻合较好。
补充资料：环形试样
分子式：
CAS号：
性质： 用于测定橡胶拉伸强度用的一种试样，试样呈环形，可以用冲切，也可用旋转裁切而得。目前比较常用的测定橡胶拉伸强度用试样为哑铃形试样，但有时会出现在标线外或夹持器处断裂，按标准规定无法求得它的拉伸强度值，此时必须采用环形试样。
CAS号：
性质： 用于测定橡胶拉伸强度用的一种试样，试样呈环形，可以用冲切，也可用旋转裁切而得。目前比较常用的测定橡胶拉伸强度用试样为哑铃形试样，但有时会出现在标线外或夹持器处断裂，按标准规定无法求得它的拉伸强度值，此时必须采用环形试样。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条