1) Polyacrylic thickener
聚丙烯酸增稠剂
2) polyacrylate thickener
聚丙烯酸盐增稠剂
1.
Solution polymerization and two different inverse emulsion polymerizations have been carried out to synthesize hydrophobically associative polyacrylate thickener.
采用溶液聚合法、反相乳液聚合法合成疏水缔合型聚丙烯酸盐增稠剂 ,比较聚合工艺和产物性能。
3) polyacrylamide thickener
聚丙烯酰胺增稠剂
1.
The amphoteric polyacrylamide thickener with salt resistance property was prepared by two-step polymerization.
采用两步聚合法,即甲基丙烯酰氧乙基三甲基氯化铵自聚得到聚电解质聚甲基丙烯酰氧乙基三甲基氯化铵(PDMC);PDMC与丙烯酸、长碳链疏水单体丙烯酸十八酯(ODA)等单体共混,以N,N’-亚甲基双丙烯酰胺(MBAM)为交联剂、过硫酸钾为引发剂进行反相乳液聚合,得到疏水缔合型具有互穿网络结构的两性聚丙烯酰胺增稠剂乳液。
4) acrylic synthetic thickener
丙烯酸型合成增稠剂
1.
The neutral one must be treated with anti-gelling agents such as sodium hexametaphosphorate,dispersant NNO and cationic surfactant 1231 Br,followed by adjusting to weakly acidic one,thus to avoid the gelling problem happening when the pigment printing carbon black meets the acrylic synthetic thickeners.
色素炭黑具有比较好的抗凝胶能力,而中性炭黑必须用抗凝剂六偏磷酸钠、扩散剂NNO、阳离子表面活性剂1231 Br进行表面处理,并把pH值调配到微酸性,以解决涂料印花炭黑遇丙烯酸型合成增稠剂会产生凝胶的问题。
5) acrylic emulsion thickener
丙烯酸乳液增稠剂
6) polymeric viscosifier
聚合增稠剂
补充资料：合成增稠剂KG-201
分子式：
CAS号：
性质：外观为淡黄色黏稠液。pH值6～7。含固量(35±2)％，表观黏度0.1～0.5Pa·s，用50倍蒸馏水稀释，旋转黏度不低于3Pa·s。主要成分是γ射线引发的丙烯酸聚合物铵盐。主要应用于涂料印花。作为增稠剂，配制少煤油或无煤油印花浆，遇电解质后增稠效果明显降低。
CAS号：
性质：外观为淡黄色黏稠液。pH值6～7。含固量(35±2)％，表观黏度0.1～0.5Pa·s，用50倍蒸馏水稀释，旋转黏度不低于3Pa·s。主要成分是γ射线引发的丙烯酸聚合物铵盐。主要应用于涂料印花。作为增稠剂，配制少煤油或无煤油印花浆，遇电解质后增稠效果明显降低。