1) Alkali aggregate corrosion
碱骨料腐蚀
1.
Alkali aggregate corrosion is caused by alkali aggregate reaction Alkali aggregate corrosion is one of the important factors which result in insufficiency of concrete durability Mechanisms and conditions of alkali aggregate corrosion are analyzed Some preventing methods and some problems in alkali aggregate corrosion are discusse
碱骨料腐蚀是一种由碱 -骨料反应引起的混凝土腐蚀 ,是导致混凝土耐久性不足的一个重要因素。
2) alkali corrosion resistance
耐碱腐蚀
1.
The assessment of coating alkali corrosion resistance was done through the measurements of weight loss and flexural strength degradation after 48h and longer exposure time in alkali vapor corrosion at 1000℃.
4ZP)涂层,采用XRD、SEM等分析手段研究了涂层的相组成和微观结构,并通过分别测定涂覆和未涂覆涂层试样在1000℃下受腐蚀后的质量损失和强度变化,对涂层的耐碱腐蚀性能进行了表征。
2.
4ZP) coating was deposited on SiC ceramic by slip dip-coating technique to improve its alkali corrosion resistance at high temperature.
4ZP)涂层,以改善其高温耐碱腐蚀性能。
3) Alkali Corrosion
碱腐蚀
1.
But the destruction of alkali corrosion to concrete materical actually reports very few, even sometimes it is wrongly considered that alkali is harmless to concrete.
碱腐蚀是一些氧化铝厂房混凝土结构耐久性不足的主要原因之一,但是关于碱溶液对混凝土可能产生的腐蚀破坏,却报道很少,甚至有时被错误地理解,认为碱对混凝土是无害的。
6) erode lye
腐蚀碱液
1.
A technology of reclaiming germanium from the chemic erode lye;
化学腐蚀碱液中锗的回收工艺
补充资料：碱骨料反应
当骨料中含有活性氧化硅颗粒时,会与水泥中的碱类发生反应,使混凝土发生不均匀膨胀,造成裂缝,强度和弹性模量下降等不良现象,从而威胁工程安全.这种现象称为碱骨料反应.
说明：补充资料仅用于学习参考，请勿用于其它任何用途。