The research showed that the difference of the specimen was influenced largely by the fines quality from 125 times gyratory compacting molding and 75 times Marshall compacting molding.
研究发现,125次旋转压实成型的试件与75次马歇尔击实成型试件的体积特性差异受细料品质影响很大,马歇尔击实和旋转压实成型有着本质的区别。
4) Marshall compaction test
马歇尔击实试验
1.
The author analyses the correlation between the standard and the large scale Marshall compaction tests by comparative study It has been found out that the large scale Marshall compaction test may enhance the compactness of bitument mixtures with conspicuous improvement of the water stability and high temperature stability of the mixture
通过标准马歇尔击实试验和大型马歇尔击实试验的对比研究 ,分析两者之间的内在关系 ,认为通过大型马歇尔击实试验可以提高沥青混合料的密实度 ,对沥青混合料的水稳定性和高温稳定性有明显改善。
5) marshall compaction method
马歇尔击实法
1.
Firstly,by using marshall compaction method and wheel-grind method to molding asphalt mixture,It was analysed in this paper that the volume parameters of the asphalt mixture including volume of air voids,voids in mineral aggregate and voids filled with asphalt.
首先,本文采用马歇尔击实法和轮碾法成型沥青混合料试件,分析比较试件的空隙率、矿料间隙率、沥青饱和度等体积参数。
2.
This paper compares and analyses the two design methods———Marshall compaction method and revolving compaction for asphalt mixture from aspects of material selection,aggregate mineral gradation design,optimum asphalt content determination and verification test.
对马歇尔击实法和旋转压实法2种沥青混合料设计方法,在材料选用、矿料合成级配设计、最佳沥青用量的确定和验证试验等方面进行对比、分析;并通过实例分析了2种设计方法的特点、差异以及在一定条件下设计结果的经验关系。