1) large porcelain insulator
大型瓷件
1.
Focusing on problems of shed dropping and under-rib crack of large porcelain insulators,it is revealed that these defects are caused by reduced moisture on shed bottom part(near body)of blanks after drying and intensive moisture absorption during glazing.
针对大型瓷件掉伞及伞内裂的问题,分析了该缺陷的产生是由于光坯伞根部位出烘水分过低及坯件上釉时吸湿过大所致。
2) giant porcelain shell
大型瓷套
3) Ceramic Mold/Investment Casting
陶瓷型/熔模铸件
4) heavy forging
大型锻件
1.
Research in the Process of Cuboid Heavy Forging;
长方体大型锻件工艺的探讨
2.
Study on Healing of Interior Crack-type Fault in Heavy Forging by Modeling;
大型锻件内裂纹缺陷修复的物理模拟研究
3.
In order to control the microstructure of heavy forgings,an optimization method based on composite design and numerical simulation was proposed.
为了对大型锻件微观组织进行控制,提出了一种基于复合设计和数值模拟的优化设计方法,优化设计以始锻温度和锻模击打速度为优化设计变量,以终锻件晶粒均匀细小为微观组织性能评价指标。
5) heavy forgings
大型锻件
1.
The Repairing Study for the Defects Inside the Heavy Forgings;
大型锻件内部缺陷的修复研究
2.
Microstructure of heavy forgings robust parameters control methodology based on taguchi method;
基于田口法的大型锻件微观组织健壮参数控制方法
3.
In order to control the microstructure and fracture of heavy forgings,a multiobjective optimization method based on numerical simulation was proposed.
为了对大型锻件多步锻造过程中微观组织和裂纹进行控制,提出了一种基于数值模拟的多目标优化设计方法。
6) large-scale injection part
大型塑件
补充资料：瓷件黏接剂
分子式：
CAS号：
性质：将分段瓷件黏接成一体的材料。通常要求粘接后瓷件接口处的机械强度、耐温度急变性能和化学稳定性等应均不逊于瓷质本身性能。黏接剂分为无机和有机两类。无机黏结剂可采用高温釉(1000℃以上)或低温釉(1000℃以下)，将其涂于瓷件的接口处，再经高温焙烧即行黏合。有机粘接剂大都采用高分子化合物如环氧树脂，并配加固化剂和瓷粉填料，混合均匀后涂在瓷件接口面上，经一定温度固化即可。有机黏结剂黏接的瓷件，在常温下的性能与无机粘接剂相似，黏结工艺简便，但使用温度受到限制，一般不超过350℃。
CAS号：
性质：将分段瓷件黏接成一体的材料。通常要求粘接后瓷件接口处的机械强度、耐温度急变性能和化学稳定性等应均不逊于瓷质本身性能。黏接剂分为无机和有机两类。无机黏结剂可采用高温釉(1000℃以上)或低温釉(1000℃以下)，将其涂于瓷件的接口处，再经高温焙烧即行黏合。有机粘接剂大都采用高分子化合物如环氧树脂，并配加固化剂和瓷粉填料，混合均匀后涂在瓷件接口面上，经一定温度固化即可。有机黏结剂黏接的瓷件，在常温下的性能与无机粘接剂相似，黏结工艺简便，但使用温度受到限制，一般不超过350℃。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条