1) anti-cracking in low temperature
抗低温开裂
2) low temperature cracking resistance
低温抗开裂性
3) low-temperature anti-crack
低温抗裂
1.
By discoursing the low-temperature anti-crack performance of asphalt mixture paved on bridge deck by means of low-temperature bending test estimating method,this paper proposes comprehensive technical parameters reflecting strength and deformation as a reference for design and construction of bridge deck pavement.
根据低温弯曲试验,对桥面铺装沥青混合料的低温抗裂性能进行评价,提出反映强度和变形的综合技术参数,供桥面铺装设计与施工参考。
4) low-temperature cracking
低温开裂
1.
Low-temperature cracking of asphalt pavement is mostly affected by low temperature performances of asphalt.
沥青的低温性能是影响沥青路面低温开裂的主要原因。
5) low temperature crack resistance
低温抗裂性
1.
Compared with basal and modified asphalt mixture,the performances of high modulus asphalt mixture,including high temperature stability,low temperature crack resistance and dynamic modulus in different temperature and variable loading frequency,are analyzed by dint of experiment and study which considers the material ingredient and designing methods.
从高模量沥青混合料的材料组成及配合比设计出发,通过与基质沥青混合料和几种改性沥青混合料路用性能的对比,利用试验方法分析了高模量沥青混合料材料的高温稳定性、低温抗裂性以及不同温度和加载频率下的动态模量。
6) low temperature anti-cracking performance
低温抗裂性
1.
To ensure low temperature anti-cracking performance of asphalt treated base,the low temperature anti-cracking performance of three kinds of aggregate graduation ATB30 were comprehensively evaluated by freeze and thaw low temperature (-15 ℃、-5 ℃、5 ℃、15 ℃) split test and low temperature(-15 ℃、-10 ℃、-5 ℃、0 ℃、5 ℃、10 ℃、15 ℃) bend test.
为了确保沥青稳定碎石基层的低温抗裂性,对3种ATB30级配进行了冻融后低温(-15℃、-5℃、5℃、15℃)劈裂试验和低温(-15℃、-10℃、-5℃、0℃、5℃、10℃、15℃)弯曲试验,全面评价了ATB30的低温抗裂性。
2.
This paper carries out the bending beam and creep deformation tests under low temperature for the different aggregate grading materials in stress absorbing layers with inventive Sampave asphalt and the other two modified asphalts and then analyzes the influences of asphalt binder and aggregate grading on low temperature anti-cracking performances.
通过对自主研发的Sampave等3种改性沥青结合料和不同级配的应力吸收层沥青混合料进行低温弯曲和低温蠕变试验,分析沥青结合料和矿料级配对应力吸收层沥青混合料低温抗裂性能的影响。
补充资料:耐低温开裂温度
分子式:
CAS号:
性质:在低温下将试样猛烈地弯折而不产生开裂的最低温度。这是高分子材料在低温使用条件下的一种实用检验,有相应的试验方法规定具体的试验条件。有一个测定软塑料片的低温对折冲击试验就是将试样对折后夹在试想样夹上,然后浸入酒精干冰的冷媒内,恒温后用一定能量的冲锤冲击试样,求其破裂率为50%时的温度。
CAS号:
性质:在低温下将试样猛烈地弯折而不产生开裂的最低温度。这是高分子材料在低温使用条件下的一种实用检验,有相应的试验方法规定具体的试验条件。有一个测定软塑料片的低温对折冲击试验就是将试样对折后夹在试想样夹上,然后浸入酒精干冰的冷媒内,恒温后用一定能量的冲锤冲击试样,求其破裂率为50%时的温度。