1) potentionstatic deposition
恒电位沉积法
2) potentiostatic deposition
恒电位沉积
3) Potentiostatic electro-deposition
恒电位电沉积
4) galvanostatic electrodeposition
恒电流沉积
1.
Pd-Ni and Pd-Ag alloy nanowires arrays have been fabricated in the nanopores of anodic aluminum oxide template with 200 nm in diameter and 60 μm in depth by galvanostatic electrodeposition.
在孔深60μm直径200 nm的通孔氧化铝模板中,采用恒电流沉积法制备了钯镍与钯银合金纳米线阵列。
5) sweep potential deposition
扫描电位沉积法
1.
Bi-Pt alloy film for detecting of small inorganic and organic molecules was prepared from a dimethylsulfoxide bath using sweep potential deposition.
采用扫描电位沉积法在-0。
6) deposition potential
沉积电位
1.
7 and [Sn~(2+)]/[S_2O_3~(2-)]=1/5 by varying the deposition potential (E) from-0.
7,离子浓度比[Sn2+]/[S2O32-]=1/5的条件下,通过调节沉积电位在-0。
2.
The relationship between the deposition potentials and the current intensities under different deposition conditions(stirring,temperature,etc.
研究了半导体ＣｄＴｅ薄膜不同阴极电沉积条件（搅拌、加温）下，沉积电位与电流密度、沉积速率的关系。
3.
The effects of deposition potential and Zn(NO3)2 concentration on the deposition process,structure and characteristics of films were also studied.
分析了Zn(NO3)2体系ZnO的电化学沉积机理及反应过程,考察了沉积电位和Zn(NO3)2浓度对沉积过程、薄膜结构及其性能的影响。
补充资料：恒电位区段法
分子式：
CAS号：
性质： 一种可以用肉眼观察的测量孔蚀特征电位的方法。将一根长约1m的不锈钢丝试样安装在一根长玻璃管内，管内充满氯化物溶液。不锈钢丝上通以恒定直流电流产生电压降。玻璃管内放入辅助电极(与钢丝平行)，在玻璃管内远离通电正端的另一端放入参比电极。将该端的电位控制在某一数值，则不锈钢丝上各点的电位为该电位数值加上钢丝上恒定电流产生的压降。试验后可观察到一段有孔蚀，一段无孔蚀，过渡点的电位即孔蚀电位，可根据该点距放置参比电极的端点的距离所计算的电压降加上控制电位值求得。
CAS号：
性质： 一种可以用肉眼观察的测量孔蚀特征电位的方法。将一根长约1m的不锈钢丝试样安装在一根长玻璃管内，管内充满氯化物溶液。不锈钢丝上通以恒定直流电流产生电压降。玻璃管内放入辅助电极(与钢丝平行)，在玻璃管内远离通电正端的另一端放入参比电极。将该端的电位控制在某一数值，则不锈钢丝上各点的电位为该电位数值加上钢丝上恒定电流产生的压降。试验后可观察到一段有孔蚀，一段无孔蚀，过渡点的电位即孔蚀电位，可根据该点距放置参比电极的端点的距离所计算的电压降加上控制电位值求得。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条