1) concrete biaxial tensile strength
混凝土双向拉伸强度
1.
In this paper we introduce the calculative formulas of the concrete biaxial tensile strength at home and abroad, and first present our proposing formula.
针对混凝土的特性，由Ｈｉｌｌ各向异性判据，还导出了由单向拉作试验结果表达的混凝土双向拉伸强度计算公式。
3) biaxial tensile strength
双向拉伸强度
1.
This paper introduces recent studies on biaxial tensile strength of portland cement concrete, which indicate that the biaxial tensile strength is 15%～30% lower than the uniaxial tensile strength.
介绍了"砼双向拉伸强度的研究近况及研究结果,即砼的双向拉伸强度比其单向拉伸强度弱化15%～30%"。
2.
The focal point of this paper is to introduce that the important results of the concrete biaxial tensile strength as well as the application of above results to the thickness design of cement concrete pavement.
主要介绍了水泥砼双向拉伸强度研究的重要结果及其在路面板厚度设计中的应用研究;通过对路面开裂、断板等病害的分析,提出了以砼双向拉伸强度为验算标准的路面板厚度设计建议。
5) concrete flexural tensile strength
混凝土弯拉强度
6) high flexural strength concrete
高弯拉强度混凝土
1.
Technical requirements of cement,aggregate,mineral admixture and additive are put forward to produce high flexural strength concrete(HFSC) used in pavement.
主要论述了高弯拉强度混凝土对水泥、集料、掺合料及外加剂等原材料的技术要求;提出路用高弯拉强度混凝土配合比设计原则与方法,并给出推荐的配合比范围;论述了高弯拉强度混凝土拌和、运输、摊铺、切缝和养护等施工过程中的技术控制要点。
补充资料：双向拉伸薄膜
分子式：
分子量：
CAS号：
性质：一种经特殊处理的塑料薄膜。是在低于薄膜熔点、高于玻璃化温度下，对厚膜或平片进行纵向和横向双向拉伸，然后在紧张状态下进行热处理收缩定型而得到的成品。用于拉抻薄膜的树脂原料有聚丙烯、聚乙烯、聚酰胺、聚酯、聚苯乙烯、聚氯乙烯等。其中以双向拉伸聚丙烯薄膜（BOPP）产量最大，其透明度可与玻璃媲美，并具有防潮、机械强度高、尺寸稳定、质轻、无毒、印刷性良好等特点。广泛用于食品、纺织品、日用品的包装材料及复合薄膜的基材、真空镀铝基材、电容器薄膜等。
分子量：
CAS号：
性质：一种经特殊处理的塑料薄膜。是在低于薄膜熔点、高于玻璃化温度下，对厚膜或平片进行纵向和横向双向拉伸，然后在紧张状态下进行热处理收缩定型而得到的成品。用于拉抻薄膜的树脂原料有聚丙烯、聚乙烯、聚酰胺、聚酯、聚苯乙烯、聚氯乙烯等。其中以双向拉伸聚丙烯薄膜（BOPP）产量最大，其透明度可与玻璃媲美，并具有防潮、机械强度高、尺寸稳定、质轻、无毒、印刷性良好等特点。广泛用于食品、纺织品、日用品的包装材料及复合薄膜的基材、真空镀铝基材、电容器薄膜等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条