1) hydrogen induced loss
氢损
1.
The mechanism and origin of hydrogen induced loss in optical fiber cables as well as detection of hydrogen escape from cable materials are preented.
该文简述了光缆中氢损的机理、氢损的来源和光缆用材料析氢量的检测 ;根据新的 IEC规范 ,介绍了相关光纤氢老化试验的程序和各种结构的光缆在不同应用环境下氢损效应评价必要性的导则。
2) Hydrogen damage
氢损伤
1.
The types of hydrogen damages of materials in refinery wet hydrogen sulfide environment and corrosion mechanisms were described and the techniques for determining the sensitivity of different materials to hydrogen damages were presented.
阐述了炼油厂湿硫化氢环境下材料氢损伤的表现形式、腐蚀机理 ,并提出判定各种材料对氢损伤敏感程度的方
2.
5 mol / L H_2SO_4 so-lution, the critical current density to cause hydrogen damage is 20 mA / cm~2.
本文采用正电子湮没技术研究了高纯Fe中的氢损伤规律,实验结果表明,在0。
3.
It was pointed out that the hydrogen damage occurred in the inner wall of the tubes due to the bad steam-water quality is the main cause of the tube explosion.
用金相试验方法分析 1号和 2号锅炉水冷壁多次爆泄情况,认为由于汽水品质不良引起管内壁氢损伤是造成管子爆泄的主要原因,并提出相应的处理意见。
3) Hydrogen bond defect
氢键缺损
4) hydrogen induced wear
氢致磨损
5) hydrogen induced damage
氢致损伤
6) Damage on hydrogen bond
氢键损伤
补充资料：氢损伤
分子式：
CAS号：
性质：由于氢原子进入金属而导致的材料性能下降。包括高温氢腐蚀和常温条件下的氢脆两种类型，其中氢脆又可表面为氢致塑性损失、氢致开裂和形成脆性氢化物相等不同形式。