1) Zn-Mn alloy coating
Zn-Mn合金镀层
1.
In order to further improve the corrosion resistance of Zn-Mn alloy coating ,the Zn-Mn alloy coating was treated by passivation.
为进一步提高Zn-Mn合金镀层的抗蚀性,采用绿色低铬钝化处理锌锰合金镀层,并对钝化条件进行优化,研究表明,Zn-Mn合金(未钝化)浸泡1200h出现红锈,经绿色低铬钝化后,5%氯化钠水溶液浸泡1500h后出现少量红锈,锌锰合金镀层经钝化后抗蚀性明显提高。
2) Zn-Cr alloy coating
Zn-Cr合金镀层
3) Zn-Al-Cr alloy coating
Zn-Al-Cr合金镀层
1.
In order to obtain chromium containing zinc alloy coating with excellent performance,mechanical plating technologies of Zn-Cr and Zn-Al-Cr alloy coatings were developed through varying the kind and amount of activator and promoter on the basis of mechanical plating technologies of Zn and Zn-Al coatings.
利用该工艺在钢基表面获得了Zn-Cr及Zn-Al-Cr合金镀层。
4) Co-Zn coating
Co-Zn合金镀层
1.
In this work, chemically precipitated nickel hydroxide powder has been surface-modified by electroless deposition of Co-Zn coatings.
结果表明,Co-Zn合金镀层可以均匀包覆在氢氧化镍颗粒表面,氢氧化镍经化学镀处理后其表面微观组织形貌发生了明显变化。
5) 55A1-Zn alloy coating
55Al-Zn合金镀层
补充资料：Mn-Zn ferrite
分子式：
分子量：
CAS号：
性质：软磁铁氧体的一种。属尖晶石型结构。由铁、锰、锌的氧化物及其盐类，采用陶瓷工艺制成。它具有高的起始导磁率。一般在1千赫至10兆赫的频率范围内使用。可制作电感器、变压器、滤波器的磁芯、磁头及天线棒。
分子量：
CAS号：
性质：软磁铁氧体的一种。属尖晶石型结构。由铁、锰、锌的氧化物及其盐类，采用陶瓷工艺制成。它具有高的起始导磁率。一般在1千赫至10兆赫的频率范围内使用。可制作电感器、变压器、滤波器的磁芯、磁头及天线棒。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条