1) material forming status matrix (MFSM)
材料成形状态矩阵
1.
A mathematical model is developed for rapid prototyping (RP) using the conglobation parameter which relates to material forming and the material forming status matrix (MFSM) to describe material changes in space using RP processes.
针对材料中对成形有重要意义的堆积参量 ,采用矩阵方法 ,提出了材料成形状态矩阵以描述材料在快速成形全过程和各个空间位置的团聚状态的变化。
2) State configuration matrix
状态构形矩阵
3) state matrix
状态矩阵
1.
Diagonalizing of state matrix using method of complex mode;
用复模态理论讨论状态矩阵对角化问题
2.
A state matrix of water quality eutophication is established by the fitting of a curve.
本文首先利用曲线拟合的方法构造出各湖泊水质富营养化的状态矩阵,然后确定各评价指标的权重,进而通过加权平均计算综合评价值,取得了水质富营养化等级评估的满意结果。
3.
During the design process of low voltage equipments using flow chart and state matrix, the distributing control functions using Karnaugh map can satisfy the demand for the design of sequential circuits with/without intermediate states.
用流图法和状态矩阵设计低压电器电路时 ,卡诺图法分配控制函数能较好满足无过渡态和有过渡态的时序电路设计 。
5) Morphology matrices
形态矩阵
补充资料：主要射出成形材料成形时应注意事项
■主要射出成形材料成形时应注意事项
品 名 注 意 事 项
PVC
聚氯乙烯
1. 产品种类范围非常广（硬质、软质、聚合物等），成型条件各有不同，从熔融至分
解之温度范围很小，尤须注意加热温度。
2. 附着水分少，但成型周期尽可能减少（50℃~60℃热风干燥）。
3. 成型机方面，与材料直接接触的部位须电镀或采用不锈钢以防热分解所产生的盐酸
侵蚀。射出压力2100kg/cm2程度。
4. 所有塑料当中必须是细心注意温度调节。
5. 浇口附近易产生流纹，故射出操作后，柱塞不要后退使浇口充分固化后再瞬间退后为宜。
6. 加热之初温不宜高，特别注意熔融情形。第二级加热温度较高，且尽可能使成形周
期缩短，比较安全。
PA
聚醯胺树脂
1. 成型温度比其它材料高，故采用油加热的成形机较适当。
2. 吸湿性大，必须充分干燥。水分对成型品的品质影响甚大（80℃热风干燥约5~6小时）。
3. 须退火以消除内部歪斜。
PP
聚丙烯
1. 同PE，但成形温度必须较高。熔融温度170℃，超过190℃则流动性大增，则毛边增加，
易产生接缝及凹入情形。
PC
聚碳酸脂
1. 吸湿性比尼龙小，但若有些微之水分存在则成型品产生其它色泽或气泡，故必须密封
干燥同时成形时也须预备干燥（120℃之温度4小时）。
2. 加热温度超过320℃时则产生热分解，成品变色，故特别注意温度调节，又成型时的温度调节也非常重要，须特别注意其最低温度、最低时间。
3. 须退火以消除内部歪斜（130℃~135℃，1小时程度为准）。