1) Y type ferrite
Y型铁氧体
2) Y-type hexagonal ferrite
Y型六角铁氧体
1.
8Fe12O22 Y-type hexagonal ferrites were prepared by solid-state reaction method.
8Fe12O22Y型六角铁氧体,研究了材料配方、制备工艺(球磨时间、缺铁量、升温速度、保温时间等)等对六角铁氧体显微结构和磁性能的影响。
3) Y-type ferrite
Y铁氧体
4) Y type hexaferrite
Y型六角晶系铁氧体
1.
The sol-gel method is adoped to synthesize the Z and Y type hexaferrite,andtheir structure and microwave absorption properties are measured.
采用溶胶-凝胶法制备出Z／Y型六角晶系铁氧体，并分别对其结构和微波波段的吸波性能进行了测试。
5) W-type ferrite
W型铁氧体
1.
Study on preparation and electromagnetic properties of W-type ferrites doped with nickel
镍掺杂W型铁氧体的制备及电磁性能研究
2.
When calcination temperature was 1250~1300℃,the product was single W-type ferrite.
结果表明,煅烧温度低于1200℃时,产物为M晶型的铁氧体;煅烧温度为1250~1300℃时,生成单一的W型铁氧体;温度1350℃时,产物中生成了少量M晶型铁氧体。
6) W-ferrite
W-型铁氧体
补充资料：磁铅石型铁氧体
分子式：
CAS号：
性质：组成为BaFel2O19与天然磁铅石Pb(Fe7.5Mn3.5Al0.5Ti0.5)O3有相似晶体结构的铁氧体。属六角晶系。其结构较复杂，可分为六种类型：其类型符号常用M，W，X，Y，Z，U及相应的化学式BaFel2O19，BaM2+2Fe12O27，BaM2+2Fe28O46，BaM2+2Fe12O22，Ba3Mn2+2Fe24O41和Ba2M+2Fel8O30来表示(式中M代表Mn，Fe，Co，Ni，Zn，Mg等二价金属离子)。这六种晶体结构之间的差别在于氧离子密集层的堆垛重复的次数和含钡出现次数的不同。这类铁氧体的特点是具有强烈的磁晶各向异性。主要用作永磁、旋磁、磁记录和超高频软磁材料。
CAS号：
性质：组成为BaFel2O19与天然磁铅石Pb(Fe7.5Mn3.5Al0.5Ti0.5)O3有相似晶体结构的铁氧体。属六角晶系。其结构较复杂，可分为六种类型：其类型符号常用M，W，X，Y，Z，U及相应的化学式BaFel2O19，BaM2+2Fe12O27，BaM2+2Fe28O46，BaM2+2Fe12O22，Ba3Mn2+2Fe24O41和Ba2M+2Fel8O30来表示(式中M代表Mn，Fe，Co，Ni，Zn，Mg等二价金属离子)。这六种晶体结构之间的差别在于氧离子密集层的堆垛重复的次数和含钡出现次数的不同。这类铁氧体的特点是具有强烈的磁晶各向异性。主要用作永磁、旋磁、磁记录和超高频软磁材料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。