1) composite electric contact
复合电触点
1.
Precious metal and its alloy rivet-type composite electric contacts must be examined for composite strength in hot state with the exceptoon of composite strength in cold state.
贵金属及其合金铆钉型复合电触点除了应考核其冷态复合强度之外,还必需增加在热态下复合强度的考核,只有这样才能满足用户在实际运行时对复合触点复合强度的要求。
2) bimetal rivet
复合铆钉触点
1.
This paper mainly analyses the forces during the process of flattening test of bimetal rivets,elaborates the reasons of edge cracking after flattening of bimetal rivets with relatively thin head thickness,brings forward preventive measures for edge cracking according to practical experiences,as reference for electrical appliance manufacturers.
通过对复合铆钉触点压扁试验过程的受力分析,阐述了钉头厚度较薄的触点压扁后边缘开裂的原因,并根据实践经验提出了预防该现象出现的措施,以供电器厂家参考。
3) relay fritting
继电器触点融合
4) relay fritting
继电器触点熔合
5) relay stack
继电器触点组合
6) composite electrocontact material
复合电接触材料
1.
In the paper stress is made on the effect of morphology of powder particles prepared by chemical coating process on the properties of a new type composite electrocontact material - Ag80 ( WC70 TiC30 )17 C3.
本文研究了化学包覆工艺对Ag_(80)(WC_(70)TiC_(30))_(17)C_3新型复合电接触材料粉体形貌和性能的影响。
补充资料：贵金属及其合金复合触点
分子式：
CAS号：
性质： 贵金属及其合金为复层，以铜为基体的双金属复合触点。节约贵金属、降低成本，而又不影响使用性能。有Ag/Cu、AgAul0/Cu、AgCdO12/Cu、AgCe0.5 /Cu、AgNi0.15/Cu、AgNil0/Cu和AgPb20/Cu等。复合触点的复层维氏硬度分别为490～800MPa，500～800MPa，600～760MPa，600～1100MPa，600～800MPa，650～850MPa和700～1200MPa。由贵金属(或其合金)丝与铜丝经复合铆钉机加工成铆钉。AgCdO12和AgNil0丝材是用粉冶-压力加工法制造；AgCdO12还可用内氧化-粉冶法制造。其他合金丝则用一般压力加工法制取。主要用在低压电器、家用电器、仪器仪表中做中小负荷的开关、继电器的电触点。
CAS号：
性质： 贵金属及其合金为复层，以铜为基体的双金属复合触点。节约贵金属、降低成本，而又不影响使用性能。有Ag/Cu、AgAul0/Cu、AgCdO12/Cu、AgCe0.5 /Cu、AgNi0.15/Cu、AgNil0/Cu和AgPb20/Cu等。复合触点的复层维氏硬度分别为490～800MPa，500～800MPa，600～760MPa，600～1100MPa，600～800MPa，650～850MPa和700～1200MPa。由贵金属(或其合金)丝与铜丝经复合铆钉机加工成铆钉。AgCdO12和AgNil0丝材是用粉冶-压力加工法制造；AgCdO12还可用内氧化-粉冶法制造。其他合金丝则用一般压力加工法制取。主要用在低压电器、家用电器、仪器仪表中做中小负荷的开关、继电器的电触点。