1) flexural fatigue property
抗折疲劳特性
1.
? In this paper,the flexural fatigue property of specially early strength repairing concrete is studied and the fatigue equations of concrete is established.
本文研究了路面超早强修补混凝土的抗折疲劳特性 ,并建立了修补混凝土的疲劳方程 ;结果表明 ,修补混凝土与普通混凝土相比 ,抗折疲劳性能提高 。
2) flexural fatigue-resistant performance
抗折疲劳性能
1.
This paper made experimental studies of the concrete flexural fatigue-resistant performance with two groups of different volume rate Fortaferro Fiber cement concrete and steel fiber cement concrete,and a group of plain concrete.
以两组不同体积掺量的辅特维纤维水泥混凝土、钢纤维水泥混凝土及一组素混凝土进行抗折疲劳试验研究,试验结果表明:掺加两种纤维的混凝土其疲劳性能都差于素混凝土;而且体积掺量越大,辅特维纤维混凝土的抗折疲劳性能越差。
3) flexural fatigue
抗折疲劳
1.
On the base of the domestic and overseas fatigue research, tests were designed and flexural fatigue life, distortion and damage evolvement properties were researched according to the basic mechanics property investigation of SFRC at low temperatures.
本文在国内外有关钢纤维混凝土疲劳特性研究的基础上,通过试验研究了低温钢纤维混凝土基本力学性能和低温下钢纤维混凝土梁抗折疲劳寿命、抗折疲劳变形特性以及损伤特性。
2.
Finally,experimental investigations were conducted on the flexural fatigue of steel fiber reinforced fly ash concrete beams.
本文在理论研究的基础上,首先,对钢纤维粉煤灰混凝土抗压强度和抗折强度进行了试验研究;其次,对钢纤维粉煤灰混凝土经过75次冻融循环后的抗压强度进行了试验研究;最后,对钢纤维粉煤灰混凝土小梁的抗折疲劳特性进行了试验研究。
4) fatigue resistance
抗疲劳性
1.
The property of high quality two-way and cubic hinge press saw class man made diamond was compared from the view of thermal stability,fatigue resistance and color.
从热稳定性、抗疲劳性及颜色等几方面特性比较高品质两面顶和六面顶产锯片级人造金刚石的性能。
2.
The outstanding properties are their high photocolourability and remarkable fatigue resistance .
其中，吲哚啉螺噁嗪是最有希望达到实用化的有机光致变色材料之一，由于这类化合物具有良好的光致变色性能，特别是具有较高的抗疲劳性和成色性，在有机光致变色镜片、光学镜片上有巨大的应用前景和商业价值。
5) fatigue property
疲劳特性
1.
The results show that test piece's thickness influences the fatigue property of micro-arc oxidation test pieces with differ.
研究表明,试件厚度影响微弧氧化后不同膜厚的试件疲劳特性,试件厚度为2mm时,膜厚10~20μm微弧氧化对试件疲劳寿命有提高;试件厚度3mm时,膜厚10~25μm,微弧氧化使试件疲劳寿命略有降低;预腐蚀疲劳实验表明,微弧氧化试件腐蚀疲劳寿命比普通阳极化试件的腐蚀疲劳寿命高。
2.
The test results show that the fatigue property curve and the cyclic stress-strain curve of LZ50 axletree steel perfectly conform to double logarithm linear relationship.
研究了LZ50车轴钢的循环相关特性,循环疲劳特性及循环应力-应变关系。
3.
Using 810 Material Test System, the fatigue property of ceramic coatings on LY12-CZ aluminum matrix material surface was investigated.
微弧氧化是一种新兴的表面改性技术,利用810MaterialTestSystem疲劳试验机,对LY12-CZ铝合金微弧氧化后疲劳特性进行了研究。
6) fatigue properties
疲劳特性
1.
Cyclic Fatigue Properties Comparison between ZA27 and ZCuSn10P1 Alloys;
ZA27和ZCuSn10P1循环应力下的疲劳特性比较
2.
The fatigue properties of high performance cellulose fiber,steel fiber,and hybrid fibers reinforced concrete are studied in the round,the effects of curing ages on fatigue behavior of fiber reinforced fly ash concrete are analyzed.
系统研究了高性能纤维素纤维、钢纤维、纤维素纤维及钢纤维混杂纤维混凝土的弯曲疲劳特性,探讨了龄期对纤维素纤维增强粉煤灰混凝土疲劳性能的影响。
3.
Because the hot and humid climate in the South China is more common, it is necessary to make a further discussion and research on the fatigue properties of asphalt pavemen in the condition of the hot and humid climate.
分析了高温潮湿条件下沥青混合料的疲劳特性。
补充资料：抗折强度
抗折强度
bending strength
kangzhe qiangdu抗折强度(bending strength)材料单位面积承受弯矩时的极限折断应力。又称抗弯强度、断裂模量。颗粒配比是否合理、气孔的大小和数量、组织结构是否均匀一致、颗粒间结合是否牢固等是决定耐火材料抗折强度大小的重要因素.提高衬火材朴的抗折强度，主要工艺手段是:改进砖料的颗料级配、加大成型压力以提高制品坯体的密度，使用优质结合剂和提高制品的烧结程度。 室温下测定的抗折强度称为常温抗折强度;当材料预先加热至某一温度并保温一定时间(通常为30min)进行抗折试验，所得强度值称为该温度下的高温抗折强度，也称热态抗折强度。(见彩图插页第n页) 在所有耐火材料中，用作转炉炉衬的镁破砖和不定形衬火材并，高温抗折强度是衡量其性能的不可缺少的指标。 测定抗折强度，中国标准《耐火制品常温抗折强度试验方法》(GB3。。1)，《耐火制品高温抗折强度试验方法》(GB 3002)，《铸锭用绝热板常温抗折强度试验方法》(Z BQ 45005)，其要点是:从被测制品上切取断面为正方形的长条试样，在抗折试验仪上进行试验，见图。 李L士2阵弃王 抗折试验装置原理图按下述公式计算抗折强度: ~3 FL、，~ 凡=份三于苍，MPa 一，Zb尸’一’-一式中R。为试样抗折强度，MPa;F为试样折断时最大载荷，N;L为下刀口之间距离，mm;b为试样断面宽度，mm;h为试样断面高度，mm。 测定易氧化材料的高温抗折强度时，加热炉内应充中性或还原性气体，或用碳质材料将试样搜盖，以避免试样氧化。 (王通荣)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。