1) secondary ettringite reaction
二次钙矾石反应
1.
At the same time the damage of secondary ettringite reaction is analyzed and the technology of using flyash and air entrained retarded high efficient water reducing agent are introduced to prevent shrinkage and thermal cracks and meet the demand of impermeability and flow property.
讨论了如何保证大体积混凝土的体积稳定性 ,分析了“二次钙矾石反应”的危害性 ,并利用粉煤灰和引气型缓凝高效减水剂来达到防止收缩、温差开裂以及抗渗、泵送等技术要求。
2) Secondary or subsequent ettringite
二次钙矾石
3) Ettringite
钙矾石
1.
Expansive Properties of Ettringite in A Mixture of Calcium Aluminate Cement, Portland Cement and β-Calcium Sulfate Hemihydrate;
铝酸钙水泥、硅酸盐水泥和β-半水石膏混合物中钙矾石的膨胀性能
2.
Effect of alkali on ettringite crystallization and solubility;
碱对钙矾石结晶及溶解性能的影响
3.
Quantitative Analysis of Ettringite in Cement Hydration Products by "Value K" Method of XRD;
水泥水化物中钙矾石的X射线定量分析
4) ettringite(AF_t)
钙矾石(AFt)
5) ettringite crystal
钙矾石晶体
6) chromium-containing ettringites
含铬钙矾石
1.
Experiments on the synthesis of chromium-containing ettringites;
几种含铬钙矾石的合成试验研究
补充资料：钙矾石
分子式：
CAS号：
性质：又称钙矾石。3CaO·Al2O3·3CaSO4，30～32H2O，结构式Cal2A1(OH)24(SO4)6·50H2O。三方晶系，晶体呈假六方针状。密度1.73g/cm3。一轴晶负光性。一轴晶晶体非常光折射率no=1.464，常光折射率ne=1.458。当钙钒石在水泥石中以局部反应形成时，其结晶压力可使水泥石或混凝土全部崩解，故称之为水泥杆菌。
CAS号：
性质：又称钙矾石。3CaO·Al2O3·3CaSO4，30～32H2O，结构式Cal2A1(OH)24(SO4)6·50H2O。三方晶系，晶体呈假六方针状。密度1.73g/cm3。一轴晶负光性。一轴晶晶体非常光折射率no=1.464，常光折射率ne=1.458。当钙钒石在水泥石中以局部反应形成时，其结晶压力可使水泥石或混凝土全部崩解，故称之为水泥杆菌。