1) ultra-fine calcium carbonate-filled NR powder
超细碳酸钙填充型粉末NR
2) ultra_fine calcium carbonate_filled powdered SBR
超细碳酸钙填充型粉末SBR
3) carbon black filled powder NR
炭黑填充型粉末NR
1.
Dysprosium-modified carbon black filled powder NR[P(NR/HAF-Dy)] was prepared by liquid-phase chemical deposition and co-precipitation,and the kinetic models for the stages of scorch delay,curing and over-cure were proposed based on the curing curve of P(NR/HAF-Dy) compounds to describe the curing reactions of P(NR/HAF-Dy) compounds with different Dy addition level.
采用液相化学沉积法和凝聚共沉法制备稀土镝掺杂炭黑填充型粉末NR[P(NR/HAF-Dy)],在分析P(NR/HAF-Dy)硫化曲线的基础上,建立了不同稀土镝用量下胶料在硫化延迟阶段、硫化及硫化返原阶段的动力学模型。
4) N330-filled powdered NR
高耐磨炭黑填充型粉末NR
1.
Study on N330-filled powdered NR (I) Powdering conditions and particle size distribution;
高耐磨炭黑填充型粉末NR研究 (I)粉末化条件与粒径分布
5) CaCO 3 powders
碳酸钙粉末
6) Ultrafine CaCO3
超细碳酸钙
1.
In order to improve the grafting and coating of polymer on ultrafine CaCO3 particles, the anchoring of 4,4’-azobis(4-cyanopentanoic acid) (ACPA) onto ultrafine CaCO3, and dispersion polymerization of methyl methacrylate (MMA) in the presence of CaCO3 anchored with azo initiator were investigated.
为了提高聚合物在超细碳酸钙粒子表面的接枝和包覆,对超细碳酸钙锚固偶氮引发剂及甲基丙烯酸甲酯(MMA)/改性碳酸钙原位分散聚合进行了研究。
2.
The effect of ultrafine CaCO3 and compatibilizer on the structures and properties of poly(butylene adipate-co-terephthalate) was investigated.
超细碳酸钙被用于改性PBAT(聚己二酸/对苯二甲酸丁二酯)。
补充资料：超细碳酸钙
分子式：CaCO3
CAS号：
性质：白色粉末。无臭。无味。密度2.45～2.50g/cm3。粒径0.01～0.08μm。比表面积10～70m2/g。在空气中稳定。几乎不溶于水，不溶于醇。由重质碳酸钙或白度>93度、含钙量>98％的方解石，经湿法研磨后压滤、烘干制得。或由石灰消化为石灰乳，用碳酸化沉淀制得。用于橡胶，提高制品的抗压强度、耐磨性和抗挤压强度。用于塑料，使制品表面光洁、平滑，代替部分PVC树脂用量。用于造纸，可提高涂布纸的光泽度、白度和不透明度，改善纸张的印刷适应性。
CAS号：
性质：白色粉末。无臭。无味。密度2.45～2.50g/cm3。粒径0.01～0.08μm。比表面积10～70m2/g。在空气中稳定。几乎不溶于水，不溶于醇。由重质碳酸钙或白度>93度、含钙量>98％的方解石，经湿法研磨后压滤、烘干制得。或由石灰消化为石灰乳，用碳酸化沉淀制得。用于橡胶，提高制品的抗压强度、耐磨性和抗挤压强度。用于塑料，使制品表面光洁、平滑，代替部分PVC树脂用量。用于造纸，可提高涂布纸的光泽度、白度和不透明度，改善纸张的印刷适应性。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。