1) spinel soft magnetic ferrite
尖晶石型软磁铁氧体
2) spinel ferrite
尖晶石型铁氧体
1.
In this paper, new methods have been overviewed for preparation of ultrafine spinel ferrite powders in recent years, including mechano-chemical synthesis, hydrothermal method, low-temperature combustion synthesis, sol-gel method, supercritical fluid drying and microemulsion mediated process et al.
综述了近年来在尖晶石型铁氧体超微粉体合成领域的一些最新研究进展,包括机械化学合成法、水热法、低温燃烧合成法、溶胶-凝胶法、超临界流体干燥法、微乳液法、喷雾干燥法及喷雾热分解法等。
2.
In this paper, through measuring the microwave-absorbing properties of the waste spinel ferrite which contained different magnetic and dielectric mediums in the frequency range of 7.
本文通过测量含有各种介质的尖晶石型铁氧体废料在7。
3) spineltype microwave ferrite
尖晶石型微波铁氧体
5) spinel ferrite
尖晶石铁氧体
1.
The single phase MnFe2O4 spinel ferrite is synthesized by a simple,environmentally friendly and cost-effective route,which uses Mn(NO3)2,Fe(NO3)3 and fresh egg white in an aqueous medium.
介绍了一种以新鲜蛋清蛋白为络合剂,用溶胶-凝胶法制备MnFe2O4尖晶石铁氧体的新方法,并探索最佳合成条件。
6) spinel cobalt ferrtte
尖晶石钴铁氧体
补充资料：尖晶石型铁氧体
分子式：
CAS号：
性质：与天然镁铝尖晶石(MgO·Al2O3)晶体结构相同的铁氧体。立方晶系。通式为:MeO·Fe2O3或MeFe2O4，其中Me通常为二价金属离子，如镁、锰、镍、锌、亚铁、钴、镉、铜离子等。相应的铁氧体称为镁铁氧体、锰铁氧体，以此类推。通式中的Me2+及Fe3+还可被两种或两种以上组合的其他阳离子所代替。如和等取代Me2+，取代Fe3+,此时只需满足电中性即可。例如镍锌系铁氧体饱和磁化强度0.23～0.5T，居里温度100～465℃，介电常数12.5。钛钴系铁氧体饱和磁化强度0.05～0.10T，居里温度175～275℃，介电常数18.0～19.1，介质损耗角正切值(3.1～4.2)×10-4。采用磁性陶瓷生产工艺制造。要求原料纯度高(化学试剂纯)，避免引入杂质，通过烧结达到致密化。它们是发展较早、应用较广的铁氧体。其中锰锌系、镍锌系铁氧体多用作软磁材料。镁锰系、锂镍系、锂锰系多用作矩磁材料。镁系、锂系铁氧体用旋磁铁氧体材料。
CAS号：
性质：与天然镁铝尖晶石(MgO·Al2O3)晶体结构相同的铁氧体。立方晶系。通式为:MeO·Fe2O3或MeFe2O4，其中Me通常为二价金属离子，如镁、锰、镍、锌、亚铁、钴、镉、铜离子等。相应的铁氧体称为镁铁氧体、锰铁氧体，以此类推。通式中的Me2+及Fe3+还可被两种或两种以上组合的其他阳离子所代替。如和等取代Me2+，取代Fe3+,此时只需满足电中性即可。例如镍锌系铁氧体饱和磁化强度0.23～0.5T，居里温度100～465℃，介电常数12.5。钛钴系铁氧体饱和磁化强度0.05～0.10T，居里温度175～275℃，介电常数18.0～19.1，介质损耗角正切值(3.1～4.2)×10-4。采用磁性陶瓷生产工艺制造。要求原料纯度高(化学试剂纯)，避免引入杂质，通过烧结达到致密化。它们是发展较早、应用较广的铁氧体。其中锰锌系、镍锌系铁氧体多用作软磁材料。镁锰系、锂镍系、锂锰系多用作矩磁材料。镁系、锂系铁氧体用旋磁铁氧体材料。