1) shaft with a transverse crack
含横向裂纹转子
2) rotor with cracks
含裂纹转子
3) transverse crack
横向裂纹
1.
Influence of Strength Matchings on the J-Integral ofWelded Joints With Transverse Cracks;
强度组配对含有横向裂纹焊接接头J积分的影响
2.
Study on causes of transverse cracks in main beam of PC cable-stayed bridge from forces analysis;
从受力角度谈PC斜拉桥主梁横向裂纹产生原因
3.
Cause analysis on transverse cracks of water-cooling wall tubes in Ningxia Dawukou Power Plant;
国电宁夏大武口发电厂水冷壁管横向裂纹原因分析
4) transverse cracking
横向裂纹
1.
The mechanism of the transverse cracking failure in water wall and causes are analyzed.
探讨锅炉水冷壁横向裂纹的机理。
2.
Temperature fluctuating of tube walls is one of the most important causes for transverse cracking failure in water walls of boilers.
针对锅炉水冷壁金属管壁温度的波动与水冷壁管横向裂纹失效，以 Ｓ Ｇ１０００ 和 Ｈ Ｇ２００８ 锅炉水冷壁壁温测量试验的结果为对象，根据不同的管壁温度波动特点，结合炉内、锅内传热分析，提出了不同的壁温波动原因：炉内不稳定结渣的脱落造成了 Ｈ Ｇ２００８ 控制循环锅炉水冷壁壁温的波动；蒸干传热恶化导致 Ｓ Ｈ１０００直流锅炉水冷壁壁温的波动。
5) transversed and longitudinal crack
纵横向裂纹
6) transverse crack
横向裂纹，横向裂缝
补充资料：转子裂纹处理
转子裂纹处理
treatment of crack in rotor
zhuonz一11ewen Chul-转子裂纹处理(treatment of eraek in rotor) 汽轮机高中压转子在高温条件下运行，承受交变热应力，使转子表面应力集中区域发生低周疲劳损伤及高温蠕变损伤，经长期运行后转子表面将出现裂纹。另外，转子在制造加工过程也会使转子表面受到损伤，留下不应有的刀痕和缺陷。这些裂纹和缺陷一经发现，就应及时消除。否则，裂纹在蒸汽介质的腐蚀作用和交变载荷作用下，将会加剧发展，导致转子破坏。 裂纹检查机组在大修时必须对转子进行检查。除宏观检查外，还应对转子中心孔和外表面进行无报检剧。如发现转子表面裂纹，应对裂纹深度及长度进行测量。 处理方法转子外表面发生微小裂纹，可用砂布打磨。中心孔表面裂纹和缺陷，可进行幢孔。对于转子应力集中区域出现较大裂纹(深度10mm左右)必须采用车削的方法。一般电厂不可能具备车削转子的大型车床，可采用低速动平衡台，另配一小型刀架就可对转子进行车削加工。对于较深裂纹转子的车削处理，要持懊重态度。车削后要进行打磨，并进行表面无损探伤，不得有微裂纹存在。另外，要对加工处理后的转子进行强度校核计算。 为保证转子的安全运行，延长其使用寿命，必须对转子裂纹部位的结构进行改进。早期生产的汽轮机汽封热槽较窄，轴肩和叶轮根部过渡圆弧角偏小，使得应力集中系数过高。故在裂纹处理时，应适当加宽汽封热槽，放大轴肩、叶轮根部过渡圆弧半径，以减小应力集中系数。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。