1) electrode-shaping
电极成形
1.
The electrode-shaping method is the key of turning the battery research results to battery products.
电极成形方法是电池研究成果转化为产品的主要关键。
2) shaped electrode
成形电极
3) beam-forming electrode
射束形成电极
4) contact diffusion
电极孔形成扩散
5) forming limit
成形极限
1.
Suitability of some ductile fracture criteria and yield criteria in forming limit prediction;
成形极限预测韧性断裂准则及屈服准则的影响
2.
The theoretical prediction and numerical simulation of sheet metal forming limit;
板料成形极限的理论预测与数值模拟研究
3.
The forming limit of forward extrusion and cross rolling tube billet;
管坯正挤—横轧的成形极限
6) forming limits
成形极限
1.
Research on the forming limits and technology application of long shaft parts in open-die extrusion;
长轴类零件开式挤压工艺应用及成形极限研究
2.
Theoretical analyses of forming limits in tube hydroforming;
圆管受轴压和充液内高压成形极限的理论解析
3.
Experimental investigation on forming limits of AA5052 sheet in hybrid quasi-static/dynamic plane-strain tensile process
AA5052板材准静态/动态平面应变成形极限试验研究
补充资料：主要射出成形材料成形时应注意事项
■主要射出成形材料成形时应注意事项
品 名 注 意 事 项
PVC
聚氯乙烯
1. 产品种类范围非常广（硬质、软质、聚合物等），成型条件各有不同，从熔融至分
解之温度范围很小，尤须注意加热温度。
2. 附着水分少，但成型周期尽可能减少（50℃~60℃热风干燥）。
3. 成型机方面，与材料直接接触的部位须电镀或采用不锈钢以防热分解所产生的盐酸
侵蚀。射出压力2100kg/cm2程度。
4. 所有塑料当中必须是细心注意温度调节。
5. 浇口附近易产生流纹，故射出操作后，柱塞不要后退使浇口充分固化后再瞬间退后为宜。
6. 加热之初温不宜高，特别注意熔融情形。第二级加热温度较高，且尽可能使成形周
期缩短，比较安全。
PA
聚醯胺树脂
1. 成型温度比其它材料高，故采用油加热的成形机较适当。
2. 吸湿性大，必须充分干燥。水分对成型品的品质影响甚大（80℃热风干燥约5~6小时）。
3. 须退火以消除内部歪斜。
PP
聚丙烯
1. 同PE，但成形温度必须较高。熔融温度170℃，超过190℃则流动性大增，则毛边增加，
易产生接缝及凹入情形。
PC
聚碳酸脂
1. 吸湿性比尼龙小，但若有些微之水分存在则成型品产生其它色泽或气泡，故必须密封
干燥同时成形时也须预备干燥（120℃之温度4小时）。
2. 加热温度超过320℃时则产生热分解，成品变色，故特别注意温度调节，又成型时的温度调节也非常重要，须特别注意其最低温度、最低时间。
3. 须退火以消除内部歪斜（130℃~135℃，1小时程度为准）。