1) water swelling rubber-plastic materials
吸水膨胀橡塑材料
1.
The development research and application of water swelling rubber-plastic materials were discussed systematically in this paper.
研究了用物理共混法制备吸水膨胀橡塑材料的一些特性 ,对在不同CPE/SBR配比下吸水膨胀橡塑材料的吸水性能和力学性能及其影响因素进行了研究。
2) water swelling rubber like plastic material
吸水膨胀性橡塑材料
1.
The water swelling rubber like plastic material(WSM) was prepared by blending chlorinated polyethylene(CPE) with sodium acrylate(AANa).
由丙烯酸钠 (AANa)与氯化聚乙烯 (CPE)制备吸水膨胀性橡塑材料 (WSM)。
3) water swelling material
吸水膨胀材料
1.
A new type of water swelling material can be prepared by adding a water absorbent A and a super water absorbed resin B into a styrene butadiene styrene (SBS) modified asphalt which contains asphalt of 100, SBS of 14 and base oil of 6 in mass fractions.
30时 ,所研制的材料吸水能力适中 ,性能优良 ,可用作吸水膨胀材料。
2.
The research development and application prospect of water swelling materials as well as their present production are introduced.
论述了吸水膨胀材料的研究进展和应用前景以及生产现状,并对其市场进行了分析和预测,建议利用我省的科研和原料优势,尽快使其实现产业化,以推动我省复合材料产业的发展。
4) water-swelling polymer material
吸水膨胀高分子材料
1.
The regulations that water-absorbed resin and reinforced filler affected volume expansibility,rigidity,tensile strength and tensile elongation of water-swelling polymer material were studied by using central composite design method.
结果表明,随着吸水树脂用量的增加,吸水膨胀高分子材料的体积膨胀率升高,而硬度、拉伸强度和扯断伸长率降低;高耐磨炭黑对吸水膨胀高分子材料具有补强作用。
5) water-swellable rubber
吸水膨胀橡胶
1.
Research progress on preparation and application of water-swellable rubber
吸水膨胀橡胶制备技术及应用研究进展
2.
The mechanism of water absorption and the preparation methods of water-swellable rubber(WSR)were introduced.
介绍了吸水膨胀橡胶(WSR)的吸水机理、制备方法及改性研究的进展,并展望了其应用前景。
3.
A water-swellable rubber has been prepared by blending with naturerubber(NR) as matrix, cross-linked sodium polyacrylate(CSP) as high-absorbent water resin the amphiphilic block copolymer poly(ethylene oxide)-b-poly(butylacrylate)(PEO-b-PBA) as compatibilizer and the poly(ethylene glycol)(PEG) as absorbent accelerant.
以天然橡胶为基体 ,微米级交联聚丙烯酸钠为高吸水性树脂 ,两亲性嵌段共聚物聚氧化乙烯 - b-聚丙烯酸丁酯 (PEO- b- PBA)为增容剂 ,聚乙二醇为吸水促进剂 ,制备了嵌段共聚物增容型吸水膨胀橡胶。
6) water swellable rubber
吸水膨胀橡胶
1.
The water swellable rubber prepared by blending NR and water absorbing agent was researched.
以天然橡胶和聚丙烯酸纳(PAANa)为主要原料,采用物理共混方式制备吸水膨胀橡胶,研究了增容剂及辅助吸水剂PEG对吸水膨胀橡胶吸水性能和力学性能的影响。
补充资料：橡塑磁性材料
橡塑磁性材料
rubber and Plastie magnetie mate-二_1一
橡塑磁性材料rubber and plastiC magnetsC mate-rials将强磁性(铁磁性和亚铁磁性等)材料制成细粉，再加橡胶或塑料(树脂)粘结剂(粉末状)混合均匀，然后加热固结或压制成的磁性材料。因采用粘结方法制成，故又称粘结磁性材料。加橡胶粉制成的橡胶磁性材料兼有弹性、柔软性和强磁性;加塑料粉制成的塑料磁性材料适用于简化热处理工艺，需要精确尺寸和复杂形状、以及不能进行高温热处理(如Sm一Fe一N系稀土永磁材料)等情况。 制备工艺首先采用粉末冶金或陶瓷方法将磁性材料制成粉末(特殊磁性材料还对磁粉的粒径和形状有一定要求)，然后与一定重量或体积配比(重量约1.5一6%或体积10一30%)的粘结剂(塑料或橡胶粉)混合均匀，经压制成型、注射成型或其他成型处理，得到一定形状和尺寸的粘结坯体，再经过一定温度(约100一400℃)和时间(约几分钟到几十小时)的固化处理，便可得到粘结磁性材料制品。有些磁性材料在成型或(和)固化时还需要进行磁场取向。在制造过程中，磁粉的制备，粘结剂和成型方法的选择，固化处理条件的确定，对于粘结磁性材料的磁性、抗氧化性、耐腐蚀性、耐热性和力学性能等都有显著影响，而磁特性一般都低于不加粘结剂的磁性材料(只有频谱特性等例外)。 粘结剂橡塑磁性材料用粘结剂主要分为热硬化性树脂(塑料)、热可塑性树脂(塑料)和橡胶。在特殊情况下可采用低熔点金属或合金作粘结剂，但要求它们与磁粉无明显化学作用。热硬化性树脂的特点是粘结力强，收缩率小，耐水性和密封性好，可在较低温度硬化，常用的有环氧树脂、酚醛树脂、聚氨酷和聚乙烯醇等;热可塑性树脂除具有热硬化性树脂的主要特点外，还有在较高温度(约200一300℃)下热流动性和热稳定性好等优点，常用的有聚酞胺、聚苯撑硫、丁二醇脂和聚对苯二甲酸等;橡胶的主要特点是弹性高，力学性能和化学稳定性好，常用的有热塑性聚氛醋橡胶(TPU)和聚烯烃橡胶(TPO)等。在一些情况下，为增加磁粉与粘结剂之间的亲和性，使磁粉表面活化，增强粘结剂在磁粉上的附着力，可加入少量祸联剂(又称促进剂)。一般祸联剂用量仅为粘结剂重量的1一2%。 种类理论上任何磁性材料都可以制成橡塑磁性材料。现有橡塑(粘结)磁性材料按磁特性主要分为3类。 ①高频粘结磁性材料:多以金属磁性细粉作磁性基损耗只有二用。料或成应钻结巳一51 但属磁狗橡狗配要用体。由于金属磁性材料在高频率下有涡流效应，使显著增加(与频率平方成比例);又由于趋肤效应，材料表面薄层参与作用，故限制了其在高频段的吏若将金属磁性材料制成细粉(磁粉)，与绝缘性的塑橡胶粉(或液体)均匀混合，经过一定处理，即可制用于高频段的粘结磁性材料。