1) CUFA
粉煤灰复合超细粉
1.
Through testing of the concrete mixed with Ultra-pulverized Fuel Ash Composite Powder(CUFA), C50 high performance concrete for road is made, and used into practice.
通过在混凝土中掺入经改性的粉煤灰复合超细粉(CUFA)的试验,配制了C50强 度级别的道路高性能混凝土,同时应用于实际工程,并通过试验室材性试验与现场工程试验相结 合,对比研究了道路高性能混凝土各方面的力学性能。
2) ultrafine fly ash slag composite
粉煤灰-矿渣复合超细粉
3) concrete with compound ultrafine fly ash
复合超细粉煤灰混凝土
4) coal ash fused fiber composite paper
粉煤灰超细纤维复合纸
5) Ultra-fine fly ash
超细粉煤灰
1.
Experimental studies on capabilities of steam curing ultra-fine fly ash high performance concrete;
蒸养超细粉煤灰高性能混凝土性能试验研究
2.
Research on integrated utilization of ultra-fine fly ash-fluorogypsum in highway repair;
超细粉煤灰-氟石膏在道路修补工程中的综合利用研究
3.
Some factors affecting early comprssive strength of steam-curing concrete with ultra-fine fly ash;
蒸养超细粉煤灰混凝土早期强度影响因素研究
6) Superfine fly ash
超细粉煤灰
1.
Fly ash based load-bearing cellular concrete has been developed by using superfine fly ash as substitute for original ash in this paper to coalesce the environment protection development in concrete materials at present.
结合目前混凝土材料向绿色高性能化发展的方向 ,以超细粉煤灰作为加气混凝土配料以替代原状粉煤灰 ,配制出符合承重要求的加气混凝土。
2.
It is experimentally tested for water reducing rate of cement paste and water-reducing mechanism,in which Superfine fly ash and superplasticizer have been added respectively or combinatively,and the Superfine fly ash is prepared by the steam gas mill.
通过对超细粉煤灰在单掺,及与高效减水剂复合掺入时的减水率进行试验研究,分析了"过热蒸汽气流磨"制备的超细粉煤灰与高效减水剂的复合减水效应及减水机理,结果表明,在不掺加高效减水剂的条件下,粒径大于10μm的超细粉煤灰对水泥浆有一定的减水增塑作用;当与高效减水剂共同作用时,二者"双掺"的减水率急剧增加,与原状低等级粉煤灰相比,磨细粉煤灰的减水作用增加明显。
3.
It is experimentally tested for water reducing rate of cement paste and water-reducing mechanism,in which superfine fly ash and superplasticizer have been added respectively or combinative,and the superfine fly ash is prepared by the steam gas mill.
通过对超细粉煤灰在单掺,及与高效减水剂复合掺入时的减水率进行试验研究,分析了"过热蒸气气流磨"制备的超细粉煤灰与高效减水剂的复合减水效应及减水机理,结果表明,在不掺加高效减水剂的条件下,粒径大于10μm的超细粉煤灰对水泥浆有一定的减水增塑作用;当与高效减水剂共同作用时,二者"双掺"的减水率急剧增加,与原状低等级粉煤灰相比,磨细粉煤灰的减水作用增加明显。
补充资料：染料细粉及超细粉
分子式：
CAS号：
性质：非水溶性染料或不易溶染料常采用的剂型。如分散染料、还原染料等对粒度及粒度分布均有一定要求，要求相对集中，过细、过粗，均对使用有不良影响。染料生产企业对本企业的产品均作了规定。这些染料产品一般多在2μm到上到4μm范围内，如对某些分散染料要求控制在1μm左右，分散性能4～5级，还原染料也与分散染料近似，故有超细粉之称。为使染料产品达到上述细度，常采用万能粉碎机或砂磨、球磨等进行粉碎。
CAS号：
性质：非水溶性染料或不易溶染料常采用的剂型。如分散染料、还原染料等对粒度及粒度分布均有一定要求，要求相对集中，过细、过粗，均对使用有不良影响。染料生产企业对本企业的产品均作了规定。这些染料产品一般多在2μm到上到4μm范围内，如对某些分散染料要求控制在1μm左右，分散性能4～5级，还原染料也与分散染料近似，故有超细粉之称。为使染料产品达到上述细度，常采用万能粉碎机或砂磨、球磨等进行粉碎。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条