1) fretting corrosion
微动腐蚀
1.
Effect of cathodal polarization on fretting corrosion behaviors in slip regime;
阴极极化对滑移区微动腐蚀行为的影响
2.
Dual-motion fretting corrosion behavior of pure titanium in Hank’s and saline solutions;
Hank’s溶液和生理盐水中纯钛的复合微动腐蚀特性
3.
The fretting corrosion tests on a plane-on-ball contact of Ti6Al4V/Si_3N_4 were examined on a hydraulic fretting tester with high precision.
采用液压高精度微动试验机,做了Ti6A l4V/Si3N4摩擦副在干态、蒸馏水和Saline溶液等3种介质中的微动腐蚀试验,用激光共焦扫描显微镜(LCSM)观察了磨痕表面形貌并测量了磨损体积。
3) fretting corrosion
微动磨损腐蚀
4) fretting
[英][fret] [美][frɛt]
咬蚀,擦伤腐蚀,微动磨损
5) micro pitting nucleus
微腐蚀点
6) pore corrosion
微孔腐蚀
1.
With the effects of humidity, corrosive gas and dust particles in the air, pore corrosion contaminant appears on the pore site on plating surface and the connector reliability is lowered.
通过对长期室内自然暴露的薄镀金样片表面的形貌、腐蚀状况以及成分分析,同时对腐蚀表面不同位置处的直流接触电阻、高频接触阻抗进行测试,从而全面分析表面微孔腐蚀对电接触性能的影响。
补充资料:微动腐蚀
分子式:
CAS号:
性质:又称摩振腐蚀。在承受载荷的两金属部件相互接触的表面上由于振动和滑动而引起的腐蚀加速现象。是磨损腐蚀的一种特殊形式。微动腐蚀发生在大气中,其原因是摩擦和振动破坏了金属表面上在大气中生成的氧化膜,使氧化加速。各种转动或承受振动的机械部件都可能发生微动腐蚀。提高金属的表面硬度及强化表面润滑作用都可减轻微动腐蚀。测量金属微动腐蚀试验装置分机械式和电磁式两种。特点为通过往复旋转、偏心旋转或电磁振荡器产生往复运动来对两个金属试件施加载荷并使两者之间产生轻微振动摩擦。试验时测量摩擦力,试件的腐蚀则采用失重法或表面轮廓记录仪来评价。