1) Pt-Co alloys
Pt-Co合金
1.
phase structure, phase transformation and intrinsic magnetic properties of Pt-Co alloys were introduced,Pt-Co alloys form a face-centered cubic phase after solution treated at high temperature,and form an ordered tetragonal phase after annealing.
在可加工永磁中,Pt-Co合金的磁性能较高,对性能起决定作用的是680℃时效,随时效时间的延长,合金的Br、Hc和(BH)max呈现不同的变化趋势。
2) Co-Pt alloy
Co-Pt合金
1.
Structure and magnetic properties of Co-Pt alloy thin films prepared by electrodeposition
电沉积法制备Co-Pt合金薄膜的结构及其磁性能
2.
Highly ordered amorphous Co-Pt alloy nanowire arrays are prepared by electrodepositing it into anodized aluminum disks with nanosized pores.
通过直流电沉积方法,以多孔阳极氧化铝(AAO)为模板,在室温下成功制备出一维非晶态Co-Pt合金纳米线有序阵列。
3.
A grate deal of research has been on the synthesis of nano-structured Co-Pt alloy films.
近年来,研究发现Co-Pt合金薄膜具有强烈的垂直磁晶各向异性、很高的矫顽力以及很好的抗氧化腐蚀能力。
3) Co/Pt alloy
Co/Pt合金
5) Pt-Fe alloy
Pt-Fe合金
6) Pt-25Ir alloy
Pt-25Ir合金
1.
The characteristic of ultrasonic nondestructive detection for Pt-25Ir alloy sheet was studied in the paper.
研究了Pt-25Ir合金薄板的超声波探伤特性。
补充资料：弥散强化Pt-5Rh 合金
分子式：
CAS号：
性质：是以PtRh5合金为基用微细二氧化锆为强化相的低铑高强度结构材料，具有高度定向排列的显微组织，抗蠕变性能大于PtRh40。室温性能：密度20.6g/cm3。.抗拉强度286.4MPa。维氏硬度913.6MPa。伸长率42%。1400℃，100h断裂应力为10.3MPa，是PtRh40的1.52倍。用内氧化和复合加工方法制成片材等。制作玻纤工业用漏板，以及工业和民用玻璃熔化坩埚，供料装置和搅拌器等。
CAS号：
性质：是以PtRh5合金为基用微细二氧化锆为强化相的低铑高强度结构材料，具有高度定向排列的显微组织，抗蠕变性能大于PtRh40。室温性能：密度20.6g/cm3。.抗拉强度286.4MPa。维氏硬度913.6MPa。伸长率42%。1400℃，100h断裂应力为10.3MPa，是PtRh40的1.52倍。用内氧化和复合加工方法制成片材等。制作玻纤工业用漏板，以及工业和民用玻璃熔化坩埚，供料装置和搅拌器等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。