1) Stress relieving annealing
消应力退火
2) stress relieving
消应
1.
The heavy duty mill housing casting made of GS-20Mn5V,weighted 400t,in which the cracks were found during the casting cleaning,in this case the repair welding must be performed as well as the entire stress relieving.
铸件清理时发现裂纹,必须进行焊补和焊后整体消应。
3) stress relieving
消应力
1.
Electromagnetic hammer which' s peening frenquency and peening stress can be regulate separately is right peening tool applied to welding stress relieving.
本文基于电磁原理和电子技术,研制了一种新型的锤击消应力工具-电磁锤。
4) vibration eliminating stress technology
振动消应
1.
Seven steel pipes were tested by vibration eliminating stress technology,and residual stress of four steel pipes among them were measured.
以广州新电视塔材质为Q390GJC的冷成型钢管消应处理为例,详细介绍了Q390GJC冷成型钢管振动消应工艺、盲孔法检测残余应力的方法及应用技术。
5) stress relieving
消应处理
1.
This paper presents in detail the assembly welding procedure & stress relieving of the penstock manifold in the trnnels.
本文详细介绍了钢岔管洞内组焊的经过和消应处理。
6) Eliminating stress by itself
自消应力
参考词条
补充资料：去应力退火
去应力退火
stress-relief annealing
quying{一tuihuo去应力退火(stress一relief annealing)将工件加热到一定温度(通常在相变温度或再结晶温度以下)，保温一段时间，然后缓慢冷却，以消除各种内应力的退火工艺。 在压力加工、铸造、焊接、热处理、切削加工和其他工艺过程中，制品可能产生内应力。多数情况下，在工艺过程结束后，金属内部将保留一部分残余应力。残余应力可导致工件破裂、变形或尺寸变化，残余应力也提高金属化学活性，在残余拉应力作用下特别容易造成晶间腐蚀破裂。因此，残余应力将影响材料的使用性能或导致工件过早失效。 进行去应力退火时，金属在一定温度作用下通过内部局部塑性变形(当应力超过该温度下材料的屈服强度时)或局部的弛豫过程(当应力小于该温度下材料的屈服强度时)使残余应力松弛而达到消除的目的。在去应力退火时，工件一般缓慢加热至较低温度(灰口铸铁为500~550℃，钢为500~650℃，有色金属合金冲压件为再结晶开始温度以下)，保持一段时间后，缓慢冷却，以防止产生新的残余应力。 去应力退火并不能完全消除工件内部的残余应力，而只是大部分消除。要使残余应力彻底消除，需将工件加热至更高温度。在这种条件下，可能会带来其他组织变化，危及材料的使用性能。 (李松瑞)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。